Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:300°C,3.00mm2 | ISO2577 | 0.90 | % |
| Shrinkage rate | TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.040 | % |
| Shrinkage rate | MD:300°C,3.00mm2 | ISO2577 | 0.23 | % |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO2577 | 0.020 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 4.0 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 1.4 | % |
| Apparent density | | ISO60 | 0.70 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending stress 4 | 3.5%Strain | ISO178/A | -- | Mpa |
| Bending stress 4 | 23°C | ISO178 | 360 | Mpa |
| Bending stress 4 | FlexuralStrainatFlexuralStrength5(23°C) | | 3.0 | % |
| Bending modulus 4 | 23°C | ISO178/A | 14000 | Mpa |
| Tensile stress | Break,23°C | ISO527-2/5 | 230 | Mpa |
| Tensile strain | Break,23°C | ISO527-2/5 | 2.6 | % |
| Tensile modulus | 23°C | ISO527-2/1 | 16000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 250 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 250 | °C |
| Vicat softening temperature | -- | ISO306/B50 | >230 | °C |
| Vicat softening temperature | -- | ISO306/B120 | >230 | °C |
| BallPressure Test | 258°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Melting temperature 5 | | ISO11357-3 | 261 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.50 | |
| Relative permittivity | 23°C,1MHz | IEC60250 | 4.00 | |
| Leakage Trace Index | SolutionA | IEC60112 | 550 | V |
| Dissipation factor | 23°C,100Hz | IEC60250 | 9E-03 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 0.015 | |
| Surface resistivity | | IEC60093 | 1E+13 | ohms |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Membrane puncture strength | --6 | ISO6603-2 | 3.60 | J |
| Membrane puncture strength | --7 | ISO6603-2 | 2.80 | J |
| Membrane piercing force | --6 | ISO6603-2 | 1160 | N |
| Membrane piercing force | --7 | ISO6603-2 | 1050 | N |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 100 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 95 | kJ/m² |
| Unscented Izod impact strength | -30°C | ISO180/1U | 85 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 85 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 246 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 600 | °C |
| Extreme Oxygen Index 9 | | ISO4589-2 | 27 | % |
| BurningBehavior10 | >1.00mm | ISO3795 | passed | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortcut | | ISO1874 | PA66,GHR,14-160,GF50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.