PA66 Durethan® AKV30 GIT H2.0 LANXESS GERMANY

141

Unit Price:
$4133 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
80MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Filler: Glass fiber reinf 30% Filler by weight
Application Areas:--
Color:--
Grade:Extrusion grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:280°C,3.00mm2	ISO2577	1.5	%
	Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO294-4	0.050	%
		Shrinkage rate	MD:280°C,3.00mm2	ISO2577	0.35	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,3.00mm3	ISO2577	0.040	%
Water absorption rate	Saturation,23°C	ISO62	5.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.0	%
Apparent density		ISO60	0.70	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break,23°C	ISO527-2/5	185	Mpa
Tensile strain	Break,23°C	ISO527-2/5	3.0	%
Tensile modulus	23°C	ASTMD638	10300	Mpa
Tensile modulus	Tensile modulus	23°C	ISO527-2/1	10600	Mpa
elongation	Break,23°C	ASTMD638	3.0	%
Bending modulus	23°C	ASTMD790	841	Mpa
bending strength	23°C	ASTMD790	290	Mpa
Tensile strength	Break,23°C	ASTMD638	179	Mpa
Bending stress 4	3.5%Strain	ISO178/A	--	Mpa
	Bending stress 4	23°C	ISO178	290	Mpa
	Bending stress 4	Bending stress 4	FlexuralStrainatFlexuralStrength5(23°C)		4.0	%
Bending modulus 4	23°C	ISO178/A	8400	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ISO306/B120	>230	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	2.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	250	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	250	°C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	135	°C
Melting temperature 5		ISO11357-3	263	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+14	ohms
Volume resistivity	23°C	IEC60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC60243-1	40	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	4.00
Leakage Trace Index	SolutionA	IEC60112	600	V
Dissipation factor	23°C,1MHz	IEC60250	0.018
Dissipation factor	Dissipation factor	23°C,100Hz	IEC60250	9E-03

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	70	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	90	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	230	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Burning wire flammability index	2.0mm	IEC60695-2-12	600	°C
Extreme Oxygen Index 7		ISO4589-2	23	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO1874	PA66,GR,14-110,GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.