PA66 Zytel® 105F BK010 DUPONT USA
128
Unit Price:$3476 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 88.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Photostability Short molding cycle Good weather resistance
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.14 | ||
| Molding shrinkage rate | ASTM D955 | 1.5(流动，3.2mm) | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 2.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.3 | % |
| MD | ISO294-4 | 1.3 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 8.5 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.7 | % | |
| Stickiness number | ISO307 | 145 | cm³/g | |
| Top out temperature | 190 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 3200 | Mpa | |
| Tensile stress | Yield | ISO527-2 | 85.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 4.3 | % |
| Nominal tensile fracture strain | ISO527-2 | 24 | % | |
| elongation at break | ASTM D638/ISO 527 | 20 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 3200 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 85 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2900 | kg·cm/cm(J/M)ft·lb/in | |
| Charpy impact strength | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | NB | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 70 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 4 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 205 | °C |
| Combustibility (rate) | UL94 | V-2 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 205 | ℃（℉） | |
| ASTM D648/ISO 75 | 70 | ℃（℉） | ||
| melting point | 263 | ℃（℉） | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
| Glass transition temperature 2 | ISO11357-2 | 60.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 240 | °C | |
| Melting temperature 2 | ISO11357-3 | 263 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 45 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | ||
| 0.71mm | IEC60695-11-10,-20 | V-2 | ||
| 1.5mm | IEC60695-11-10,-20 | V-2 | ||
| Extreme Oxygen Index | ISO4589-2 | 27 | % | |
| FMVSS flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 0.0 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 6.60 | µgC/g | |
| Odor | VDA270 | 2.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.