PA66 Grilon® TS-V0 BK EMS-CHEMIE SWITZERLAND
141
- Unit Price:
- $4472 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Thermal stability
- Application Areas:Automotive Applications Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 干燥｜0.80 | % |
| MD | ISO 294-4 | 干燥｜0.70 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 干燥｜8.0 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 干燥｜2.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | 干燥｜85 | Mpa | |
| Yield | 调节后｜50 | Mpa | ||
| Break | ISO 527-2 | 干燥｜75 | Mpa | |
| Break | ISO 527-2 | 调节后｜50 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 干燥｜4.0 | % |
| Break | ISO 527-2 | 调节后｜15 | % | |
| Tensile modulus | ISO 527-2 | 干燥｜3600 | Mpa | |
| ISO 527-2 | 调节后｜1600 | Mpa | ||
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 干燥｜3.0 | kJ/m² |
| -30°C | ISO 179/1eA | 调节后｜3.0 | kJ/m² | |
| 23°C | ISO 179/1eA | 干燥｜4.0 | kJ/m² | |
| 23°C | ISO 179/1eA | 调节后｜15 | kJ/m² | |
| Nominal tensile fracture strain | ISO 527-2 | 干燥｜10 | % | |
| ISO 527-2 | 调节后｜＞50 | % | ||
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 干燥｜70 | kJ/m² |
| -30°C | ISO 179/1eU | 调节后｜- | kJ/m² | |
| 23°C | ISO 179/1eU | 干燥｜75 | kJ/m² | |
| 23°C | ISO 179/1eU | 调节后｜100 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Continuous use temperature | --3 | ISO 2578 | 干燥｜100 到120 | °C |
| --4 | 内部方法 | 干燥｜200 | °C | |
| Melting temperature 5 | ISO 11357-3 | 干燥｜260 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 干燥｜7.0E-5 | cm/cm/°C |
| TD | ISO 11359-2 | 干燥｜9.0E-5 | cm/cm/°C | |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/A | 干燥｜210 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/C | 干燥｜70 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 调节后｜1.0E+10 | ohms | |
| Volume resistivity | IEC 60093 | 干燥｜1.0E+13 | ohms·cm | |
| IEC 60093 | 调节后｜1.0E+11 | ohms·cm | ||
| Dissipation factor | 100 Hz | 干燥｜5.0E-3 | ||
| 100 Hz | 调节后｜0.15 | |||
| 1 MHz | 干燥｜0.015 | |||
| 1 MHz | 调节后｜0.070 | |||
| Dielectric strength | IEC 60243-1 | 干燥｜28 | KV/mm | |
| IEC 60243-1 | 调节后｜26 | KV/mm | ||
| Relative permittivity | 100 Hz | 干燥｜3.00 | ||
| 100 Hz | 调节后｜8.00 | |||
| 1 MHz | 干燥｜3.00 | |||
| 1 MHz | 调节后｜4.00 | |||
| Leakage Trace Index | IEC 60112 | 调节后｜660 | V |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-2 | 干燥｜35 | ||
| Flammability level | 0.40 mm | IEC 60695-11-10, -20 | 干燥｜V-0 | |
| 1.5 mm | IEC 60695-11-10, -20 | 干燥｜V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.