PA66 D.AKV30H2.0 LANXESS USA

124

Unit Price:
$3465 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
44.8MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Filler: LANXESS Germany
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		ISO60	0.70	g/cm³
Shrinkage rate	TD:290°C,2.00mm2	ISO294-4	0.93	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO294-4	0.13	%
		Shrinkage rate	MD:290°C,2.00mm2	ISO294-4	0.39	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO294-4	0.070	%
Water absorption rate	Saturation,23°C	ISO62	5.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.0	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus 4	23°C	ASTMD638	9170	Mpa
Tensile modulus	23°C	ISO527-2/1	10000	Mpa
Tensile strength	Break,23°C	ASTMD638	170	Mpa
Tensile stress	Break,23°C	ISO527-2/5	175	Mpa
elongation	Break,23°C	ASTMD638	3.0	%
Tensile strain	Break,23°C	ISO527-2/5	3.0	%
Nominal tensile fracture strain	23°C	ISO527-2/50	4.4	%
Bending modulus	23°C	ASTMD790	8690	Mpa
Bending modulus 5	23°C	ISO178/A	9200	Mpa
bending strength	23°C	ASTMD790	270	Mpa
Bending stress 5	3.5%Strain	ISO178/A	265	Mpa
	Bending stress 5	23°C	ISO178	270	Mpa
	Bending stress 5	Bending stress 5	FlexuralStrainatFlexuralStrength6(23°C)		4.0	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ASTMD648	>249	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	250	°C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTMD648	>249	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	>240	°C
Vicat softening temperature	--	ISO306/B50	230	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	>230	°C
BallPressure Test	253°C	IEC60695-10-2	Pass
Melting temperature 5		ISO11357-3	263	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	9E-05	cm/cm/°C
RTIElec	0.75mm	UL746	125	°C
RTIElec	RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	0.75mm	UL746	90.0	°C
Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	1.5mm	UL746	105	°C
RTIStr	0.75mm	UL746	110	°C
RTIStr	RTIStr	1.5mm	UL746	115	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity	23°C	IEC60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC60243-1	35	KV/mm
Dielectric strength	Dielectric strength	23°C,3.00mm	IEC60243-1	30	KV/mm
Dielectric constant 10	23°C,50Hz	IEC60250	4.00
Dielectric constant 10	Dielectric constant 10	23°C,1MHz	IEC60250	4.00
Relative permittivity	23°C,100Hz	IEC60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	4.00
Dissipation factor	23°C,50Hz	IEC60250	0.012
	Dissipation factor	23°C,100Hz	IEC60250	0.012
	Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	0.0190.019
Leakage Trace Index	SolutionA	IEC60112	475	V

film	Test Condition	Test Method	Test Result	Unit
Membrane puncture strength	--7	ISO6603-2	2.80	J
Membrane puncture strength	Membrane puncture strength	--8	ISO6603-2	2.30	J
Membrane piercing force	--7	ISO6603-2	900	N
Membrane piercing force	Membrane piercing force	--8	ISO6603-2	800	N

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	75	kJ/m²
Unscented Izod impact strength	-30°C	ISO180/1U	55	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	60	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	220	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	1.6mm	UL94	HB
			UL flame retardant rating	3.0mm	UL94	HB
			UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Burning wire flammability index	0.8mm	IEC60695-2-12	700	°C
	Burning wire flammability index	1.6mm	IEC60695-2-12	700	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	700	°C
Extreme Oxygen Index 11		ISO4589-2	23	%
BurningBehavior12	>1.00mm	ISO3795	passed

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO1874	PA66,GHR,14-100,GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.