PA66 D.AKV30H2.0 BK LANXESS USA
107
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: LANXESS Germany
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.70 | g/cm³ | |
| Shrinkage rate | TD:290°C,2.00mm2 | ISO294-4 | 0.93 | % |
| TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.13 | % | |
| MD:290°C,2.00mm2 | ISO294-4 | 0.39 | % | |
| MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 5.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 4 | 23°C | ASTMD638 | 9170 | Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 10000 | Mpa |
| Tensile strength | Break,23°C | ASTMD638 | 170 | Mpa |
| Tensile stress | Break,23°C | ISO527-2/5 | 175 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | 4.4 | % |
| Bending modulus | 23°C | ASTMD790 | 8690 | Mpa |
| Bending modulus 5 | 23°C | ISO178/A | 9200 | Mpa |
| bending strength | 23°C | ASTMD790 | 270 | Mpa |
| Bending stress 5 | 3.5%Strain | ISO178/A | 265 | Mpa |
| 23°C | ISO178 | 270 | Mpa | |
| FlexuralStrainatFlexuralStrength6(23°C) | 4.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 250 | °C | |
| 1.8MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | >240 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 230 | °C |
| -- | ISO306/B120 | >230 | °C | |
| BallPressure Test | 253°C | IEC60695-10-2 | Pass | |
| Melting temperature 5 | ISO11357-3 | 263 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| RTIElec | 0.75mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 90.0 | °C |
| 1.5mm | UL746 | 105 | °C | |
| RTIStr | 0.75mm | UL746 | 110 | °C |
| 1.5mm | UL746 | 115 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
| 23°C,3.00mm | IEC60243-1 | 30 | KV/mm | |
| Dielectric constant 10 | 23°C,50Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Dissipation factor | 23°C,50Hz | IEC60250 | 0.012 | |
| 23°C,100Hz | IEC60250 | 0.012 | ||
| 23°C,1MHz | IEC60250 | 0.0190.019 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 475 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | --7 | ISO6603-2 | 2.80 | J |
| --8 | ISO6603-2 | 2.30 | J | |
| Membrane piercing force | --7 | ISO6603-2 | 900 | N |
| --8 | ISO6603-2 | 800 | N |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 60 | kJ/m² |
| 23°C | ISO179/1eU | 75 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 220 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 1.6mm | UL94 | HB | ||
| 3.0mm | UL94 | HB | ||
| 3.2mm | UL94 | HB | ||
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 700 | °C |
| 1.6mm | IEC60695-2-12 | 700 | °C | |
| 3.0mm | IEC60695-2-12 | 700 | °C | |
| Extreme Oxygen Index 11 | ISO4589-2 | 23 | % | |
| BurningBehavior12 | >1.00mm | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA66,GHR,14-100,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.