PA66 Grilon® TSG-30/4 V0 EMS-CHEMIE SWITZERLAND
123
- Unit Price:
- $9046 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Glass fiber reinforced
- Application Areas:Automotive Applications
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 干燥｜0.70 | % |
| MD | ISO 294-4 | 干燥｜0.20 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 干燥｜4.0 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 干燥｜1.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO 2039-1 | 干燥｜255 | Mpa | |
| ISO 2039-1 | 调节后｜130 | Mpa | ||
| Tensile modulus | ISO 527-2 | 干燥｜10500 | Mpa | |
| ISO 527-2 | 调节后｜6500 | Mpa | ||
| Tensile stress | Break | ISO 527-2 | 干燥｜150 | Mpa |
| Break | ISO 527-2 | 调节后｜90.0 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 干燥｜2.5 | % |
| Break | ISO 527-2 | 调节后｜4.5 | % | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 干燥｜9.0 | kJ/m² |
| -30°C | ISO 179/1eA | 调节后｜8.5 | kJ/m² | |
| 23°C | ISO 179/1eA | 干燥｜9.5 | kJ/m² | |
| 23°C | ISO 179/1eA | 调节后｜14 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 干燥｜60 | kJ/m² |
| -30°C | ISO 179/1eU | 调节后｜60 | kJ/m² | |
| 23°C | ISO 179/1eU | 干燥｜65 | kJ/m² | |
| 23°C | ISO 179/1eU | 调节后｜70 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 干燥｜235 | °C |
| 8.0 MPa, Unannealed | ISO 75-2/C | 干燥｜165 | °C | |
| Continuous use temperature | --3 | ISO 2578 | 干燥｜100 到120 | °C |
| --4 | 内部方法 | 干燥｜220 | °C | |
| Melting temperature 5 | ISO 11357-3 | 干燥｜260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 调节后｜1.0E+10 | ohms | |
| Volume resistivity | IEC 60093 | 干燥｜1.0E+12 | ohms·cm | |
| IEC 60093 | 调节后｜1.0E+12 | ohms·cm | ||
| Dielectric strength | IEC 60243-1 | 干燥｜28 | KV/mm | |
| IEC 60243-1 | 调节后｜26 | KV/mm | ||
| Leakage Trace Index | IEC 60112 | 调节后｜600 | V |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.8 mm | IEC 60695-11-10, -20 | 干燥｜V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.