Material Description
Technical Data Sheet
Material Description
- Material Properties:Creep resistance Fatigue resistance high strength High rigidity Filler: Glass fiber reinf Enhanced strength and rig Glass fiber content is 43 43% filler by weight
- Application Areas:Gear lever Electrical/Electronic App Electrical field Electronic field Engine hood parts component Mechanical and electrical Parts under the hood of a Automotive parts Automotive sector Application in the automo Like radiator water tank Like a micro electric mot
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Wear rate | 湿 | ASTM D-1044 | 19 | ×10-6kg/1000times |
| Shrinkage rate | 干 | 旭化成方法 | 0.3/0.7 | % |
| TD | 内部方法 | 0.70 | % | |
| MD | 内部方法 | 0.30 | % | |
| 吸水率(Saturation,23°C) | 内部方法 | -- | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | -- | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 12700 | Mpa |
| Tensile strength | ASTMD638 | 196 | Mpa | |
| Tensile stress | Break,23°C | ISO527-2 | 207 | Mpa |
| elongation | Break | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | ASTMD790 | 11800 | Mpa | |
| 23°C | ISO178 | 11700 | Mpa | |
| bending strength | ASTMD790 | 314 | Mpa | |
| Bending stress | 23°C | ISO178 | 303 | Mpa |
| Taber abraser | 1000Cycles | ASTMD1044 | -- | mg |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 3(4) | % |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 11.8(8.3) | GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 118(-) | R scale |
| Flexural strength | 干(湿) | ASTM D-790 | 314(235) | Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 196(157) | Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 96(80) | M Scale |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 127(206) | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | 干 | UL 94 | HB | |
| Thermal conductivity | 干 | 0.4 | W/(m.K) | |
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 260 | °C |
| Linear expansion coefficient | 干 | ASTM D-696 | 3 | ×10-5/K |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 250 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 255 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 3E-05 | cm/cm/°C |
| thermal conductivity | 0.40 | W/m/K | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 260 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 260 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 250 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+15 | ohms | |
| IEC60093 | 1E+15 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| 23°C | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | ASTMD149 | 30 | KV/mm | |
| IEC60243-1 | 30 | KV/mm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 84 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 96 | |
| R-Sale | ASTMD785 | 118 | ||
| M-Sale | ISO2039-2 | 96 | ||
| R-Sale | ISO2039-2 | 118 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 1.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.