PA66 Zytel® 70G50HSLR BK509 DUPONT SHENZHEN
147
Unit Price:$3760 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Dimensional stability
- Application Areas:Electrical applications Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 横向流量 | ISO 294-4 | 0.80 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| 吸水率 | 饱和, 23°C, 2.00 mm | ISO 62 | 4.2 | % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.2 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 90 | kJ/m² |
| 23°C | ISO 179/1eU | 100 | kJ/m² | |
| 拉伸蠕变模量 | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| 拉伸模量 | ISO 527-2 | 17000 | Mpa | |
| 拉伸强度 | 断裂 | ISO 527-2 | 250 | Mpa |
| 伸长率 | 断裂 | ISO 527-2 | 2.3 | % |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化点 | ISO 306/B50 | 255 | °C | |
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 262 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 260 | °C | |
| 熔融温度 | ISO 11357-3 | 262 | °C | |
| 线性热膨胀系数 | 流动 | ISO 11359-2 | 1.5E-5 | cm/cm/°C |
| 横向 | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| 导热系数 | 0.46 | W/m/K | ||
| 玻璃转化温度 | ISO 11357-2 | 80.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC 62631-3-2 | -- | ohms | |
| 体积电阻率 | IEC 62631-3-1 | 1.0E+13 | ohms·m |
| 充模分析 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体密度 | 1.40 | g/cm³ | ||
| 顶出温度 | 210 | °C | ||
| Specific Heat Capacity of Melt | 1870 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.31 | W/m/K | ||
| Odor | VDA 270 | 3.00 | ||
| Emission of Organic Compounds | VDA 277 | 6.50 | µgC/g |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 | °C | ||
| 干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.20 | % | ||
| 加工（熔体）温度 | 285 到 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| 模具温度 | 50 到 90 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| 保压 | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS 可燃性 | FMVSS 302 | SE | ||
| 雾化 - G-value (condensate) | ISO 6452 | 4.0E-4 | g | |
| 极限氧指数 | ISO 4589-2 | 24 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.