PA66 Zytel® 103HSL BKB080 DUPONT USA

124

Unit Price:
$5604 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant heat-resisting Thermal stability
Application Areas:Electronic field Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	2.6	%
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO62	8.5	%
Shrinkage rate	MD	ISO294-4	1.3	%
Shrinkage rate	Shrinkage rate	TD	ISO294-4	1.3	%
MediumDensity			0.980	g/cm³
Top out temperature			190	°C
SpecificHeatCapacity of Melt			2790	J/kg/°C
ThermalConductivityofMelt			0.16	W/m/K
Stickiness number		ISO307	145	cm³/g
Density/specific gravity		ISO1183	1.14	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
TensileCreepModule	1hr	ISO899-1	--	Mpa
Nominal tensile fracture strain		ISO527-2	20	%
Tensile creep modulus	1000hr	ISO899-1	--	Mpa
Tensile stress	Yield	ISO527-2	85.0	Mpa
Tensile strain	Yield	ISO527-2	4.5	%
Tensile modulus		ISO527-2	3100	Mpa
Bending modulus		ISO178	2800	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	200	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	70.0	°C
Linear coefficient of thermal expansion	TD	ISO11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO11359-2	1E-04	cm/cm/°C
Vicat softening temperature		ISO306/B50	240	°C
Melting temperature 2		ISO11357-3	262	°C
Glass transition temperature 2		ISO11357-2	60.0	°C
EffectiveThermalDiffusivity			5E-08	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Compared to the anti leakage trace index	3.00mm	UL746	PLC0
Relative permittivity	1MHz	IEC60250	3.50
Relative permittivity	Relative permittivity	100Hz	IEC60250	3.80
Leakage Trace Index		IEC60112	600	V
Dielectric strength		IEC60243-1	31	KV/mm
Dissipation factor	100Hz	IEC60250	7.5E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.017
Volume resistivity		IEC60093	1E+15	ohms·cm

film	Test Condition	Test Method	Test Result	Unit
Tensile strain MD	Yield	ISO527-3	4.5	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	400kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Unscented Izod impact strength	-30°C	ISO180/1U	300kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	NoBreak
Charpy Notched Impact Strength	-30°C	ISO179/1eA	4.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	5.5	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO180/1A	5.5	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO180/1A	6.0	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180/1A	5.0	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.71mm	UL94	V-2
	UL flame retardant rating	1.5mm	UL94	V-2
		UL flame retardant rating	0.71mm	IEC60695-11-10,-20	V-2
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	V-2
Extreme Oxygen Index		ISO4589-2	28	%
FMVSS flammability		FMVSS302	SE

Supplementary Information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	2.10	µgC/g
Odor		VDA270	2.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.