PA66 Durethan® AKV30H1.0-NC LANXESS GERMANY
229
Unit Price:$3413 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 87MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 30% Filler by weight
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molding shrinkage rate | ASTM D955 | 0.353) | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.70 | g/cm³ | |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO2577 | 1.5 | % |
| TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.050 | % | |
| MD:280°C,3.00mm2 | ISO2577 | 0.35 | % | |
| MD:120°C,2hr,3.00mm3 | ISO2577 | 0.040 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 5.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ASTMD638 | 10300 | Mpa |
| 23°C | ISO527-2/1 | 10600 | Mpa | |
| ASTM D638/ISO 527 | 10600-7000 | kg/cm²(MPa)[Lb/in²] | ||
| tensile strength | ASTM D638/ISO 527 | 185-120 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 8400-5900 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 290-200 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile strength | Break,23°C | ASTMD638 | 179 | Mpa |
| Tensile stress | Break,23°C | ISO527-2/5 | 185 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| Bending modulus | 23°C | ASTMD790 | 841 | Mpa |
| Bending modulus 4 | 23°C | ISO178/A | 8400 | Mpa |
| bending strength | 23°C | ASTMD790 | 290 | Mpa |
| Bending stress 4 | 3.5%Strain | ISO178/A | -- | Mpa |
| 23°C | ISO178 | 290 | Mpa | |
| FlexuralStrainatFlexuralStrength5(23°C) | 4.0 | % | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 3.0-6.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 1.36 | ℃（℉） | |
| melting point | 263 | ℃（℉） | ||
| vicat softening point | ASTM D1525/ISO R306 | >230 | ℃（℉） | |
| Vicat softening temperature | ISO306/B120 | >230 | °C | |
| Melting temperature 5 | ISO11357-3 | 263 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 250 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 250 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 135 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257/IEC 60093 | 10 14(10 13) | Ω | |
| Arc resistance | ASTM D495/IEC 60112 | 40(35) | ||
| Volume resistivity | ASTM D257/IEC 60093 | 10 13(10 11) | Ω.cm | |
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 9E-03 | |
| 23°C,1MHz | IEC60250 | 0.018 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold temperature | 80 | °C | ||
| Melt Temperature | 290 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 90 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 230 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.2mm | UL94 | HB | ||
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 600 | °C |
| Extreme Oxygen Index 7 | ISO4589-2 | 23 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA66,GR,14-110,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.