PA66 Zytel® 80G14AHS-BK099 DUPONT USA
107
- Unit Price:
- $4762 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 118.875MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Thermal stability Filler: Glass fiber reinf 14% filler by weight
- Application Areas:Electrical applications small home appliances
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.90 | % |
| MD | ISO294-4 | 0.70 | % | |
| Density/specific gravity | ISO1183 | 1.19 | g/cm³ | |
| Top out temperature | 210 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO527-2 | 110 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.8 | % |
| Tensile modulus | ISO527-2 | 5000 | Mpa | |
| Bending modulus | ISO178 | 4400 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 258 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 240 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 4E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9.7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.4E-04 | cm/cm/°C | |
| Melting temperature 2 | ISO11357-3 | 263 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 13 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 13 | kJ/m² | |
| Unscented Izod impact strength | 23°C | ISO180/1U | 55 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 70 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index 4 | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.90 | µgC/g | |
| Odor | VDA270 | 4.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.