Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 干 | 旭化成方法 | 0.3/0.7 | % |
| Shrinkage rate | TD | 内部方法 | 0.70 | % |
| Shrinkage rate | MD | 内部方法 | 0.30 | % |
| Shrinkage rate | 吸水率(Saturation,23°C) | 内部方法 | -- | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | -- | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2 | 12200 | Mpa |
| Tensile strength | | ASTMD638 | 186 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 200 | Mpa |
| elongation | Break | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | | ASTMD790 | 11000 | Mpa |
| Bending modulus | 23°C | ISO178 | 10600 | Mpa |
| bending strength | | ASTMD790 | 304 | Mpa |
| Bending stress | 23°C | ISO178 | 290 | Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 186(132) | Mpa |
| Flexural strength | 干(湿) | ASTM D-790 | 304(177) | Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 118(-) | R scale |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 11.0(5.9) | GPa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 147(226) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 93(-) | M Scale |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 3(4) | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 250 | °C |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 240 | °C |
| Flame retardancy | 干 | UL 94 | HB | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 230 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 250 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 245 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 240 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTMD257 | 1E+15 | ohms |
| Surface resistivity | | IEC60093 | 1E+15 | ohms |
| Volume resistivity | | ASTMD257 | 1E+15 | ohms·cm |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | | ASTMD149 | 32 | KV/mm |
| Dielectric strength | | IEC60243-1 | 32 | KV/mm |
| Leakage Trace Index | 3.00mm | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 99 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ASTMD785 | 93 | |
| Rockwell hardness | R-Sale | ASTMD785 | 118 | |
| Rockwell hardness | M-Sale | ISO2039-2 | 93 | |
| Rockwell hardness | R-Sale | ISO2039-2 | 118 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 0.75mm | UL94 | HB | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture absorption rate | 湿 | | 1.6 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.