PA66 Leona™ FG173 BK ASAHI JAPAN

138

Unit Price:
$4263 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
201MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced Filler: Glass fiber reinf Glass fiber content is 30 Flame retardant grade UL9
Application Areas:Electrical/Electronic App Electrical components Joint switch Electrical field Electronic field Joint switch Hose switch Connector Other electrical and elec
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Wear rate	湿	ASTM D-1044	29
Shrinkage rate	TD	内部方法	0.70	%
	Shrinkage rate	MD	内部方法	0.30	%
	Shrinkage rate	Shrinkage rate	吸水率(Saturation,23°C)	内部方法	--	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	--	%
Shrinkage rate	干	旭化成方法	0.3-0.7	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	11700	Mpa
Tensile strength		ASTMD638	167	Mpa
Tensile stress	Break,23°C	ISO527-2	174	Mpa
elongation	Break	ASTMD638	2.5	%
Tensile strain	Break,23°C	ISO527-2	2.0	%
Bending modulus		ASTMD790	10800	Mpa
Bending modulus	Bending modulus	23°C	ISO178	10300	Mpa
bending strength		ASTMD790	250	Mpa
Bending stress	23°C	ISO178	259	Mpa
Taber abraser	1000Cycles	ASTMD1044	--	mg
Flexural strength	干(湿)	ASTM D-790	250(221)	Mpa
Fracture elongation rate	干(湿)	ASTM D-638	2.5(2.7)	%
Cantilever beam notch impact strength	干(湿)	ASTM D-256	88(98)	J/m
Scratch resistance coefficient	干(湿)	ASTM D-790	10.8(8.3)	GPa
tensile strength	干(湿)	ASTM D-638	167(142)	Mpa
Rockwell hardness	干(湿)	ASTM D-785	100(60)	M Scale

Thermal performance	Test Condition	Test Method	Test Result	Unit
Flame retardancy	干	UL 94	V-0
Linear expansion coefficient	干	ASTM D-696	3
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	260	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	262	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	252	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	245	°C
Linear coefficient of thermal expansion	MD	ASTMD696	3E-05	cm/cm/°C
Hot deformation temperature	1.82MPa,干	ASTM D-648	252	°C
Hot deformation temperature	Hot deformation temperature	0.46MPa,干	ASTM D-648	260	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		ASTMD149	28	KV/mm
Dielectric strength	Dielectric strength		IEC60243-1	28	KV/mm
Leakage Trace Index	3.00mm	IEC60112	275	V
Surface resistivity		ASTMD257	1E+14	ohms
Surface resistivity	Surface resistivity		IEC60093	1E+14	ohms
Volume resistivity		ASTMD257	1E+15	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch		ISO179	50	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTMD785	100
Rockwell hardness	Rockwell hardness	M-Scale	ISO2039-2	100

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	0.75mm	UL94	V-0
Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C

Basic performance	Test Condition	Test Method	Test Result	Unit
Moisture absorption rate	湿		0.6	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.