PA66 Zytel® 70G33HS1L BK031 DUPONT KOREA
128
- Unit Price:
- $3074 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability high strength Glass fiber reinforced
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.1 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Water absorption rate | Saturation, 23°C, 2.00 mm | ISO 62 | 5.7 | % |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.8 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11000 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 200 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Bending modulus | ISO 178 | 9500 | Mpa | |
| Bending stress | ISO 178 | 280 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 261 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 252 | °C | |
| Melting temperature 3 | ISO 11357-3 | 262 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 1.8E-5 | cm/cm/°C |
| Flow : -40 to 23°C | ISO 11359-2 | 2.4E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 1.3E-5 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 8.3E-5 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.4E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | ||
| Leakage Trace Index | IEC 60112 | 400 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 210 | °C | ||
| Emission of Organic Compounds | VDA 277 | 10.0 | µgC/g | |
| Odor | VDA 270 | 3.00 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 275 到 295 | °C | ||
| Melt Temperature, Optimum | 285 | °C | ||
| Mold temperature | 70 到 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00 mm | ISO 3795 | 28 | mm/min |
| UL flame retardant rating | 0.75 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS flammability | FMVSS 302 | B | ||
| 雾化 - G-value (condensate) | ISO 6452 | 6.0E-4 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.