PA66 Zytel®  70G33HS1L BK DUPONT JAPAN

127
  • Unit Price:
    $3074 USD/MT
  • Packaging Specification:
    25 KG/PKG
  • Supply Quantity:
    20MT
  • Delivery Terms:
    FOB
  • Port of Loading:
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View
serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description
Technical Data Sheet

Material Description

  • Material Properties:Thermal stability high strength Glass fiber reinforced
  • Application Areas:Automotive sector
  • Color:--
  • Grade:Enhanced level

Technical Data Sheet Compare

physical property Test ConditionTest MethodTest ResultUnit
Shrinkage rateAcross FlowISO 294-41.1%
Shrinkage rate流量ISO 294-40.30%
Water absorption rateSaturation, 23°C, 2.00 mmISO 625.7%
Water absorption rateEquilibrium, 23°C, 2.00 mm, 50% RHISO 621.8%
Mechanical performanceTest ConditionTest MethodTest ResultUnit
Tensile modulusISO 527-211000Mpa
Tensile stressBreakISO 527-2200Mpa
Tensile strainBreakISO 527-23.0%
Bending modulusISO 1789500Mpa
Bending stressISO 178280Mpa
Thermal performanceTest ConditionTest MethodTest ResultUnit
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B261°C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A252°C
Melting temperature 3ISO 11357-3262°C
Linear coefficient of thermal expansionFlowISO 11359-21.8E-5cm/cm/°C
Linear coefficient of thermal expansionFlow : -40 to 23°CISO 11359-22.4E-5cm/cm/°C
Linear coefficient of thermal expansionFlow : 55 to 160°CISO 11359-21.3E-5cm/cm/°C
Linear coefficient of thermal expansionAcross FlowISO 11359-28.3E-5cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 23°CISO 11359-26.5E-5cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 55 to 160°CISO 11359-21.4E-4cm/cm/°C
Electrical performanceTest ConditionTest MethodTest ResultUnit
Compared to the Leakage Tracking Index (CTI)UL 746PLC 1
Leakage Trace IndexIEC 60112400V
Filling analysisTest ConditionTest MethodTest ResultUnit
Top out temperature210°C
Emission of Organic CompoundsVDA 27710.0µgC/g
OdorVDA 2703.00
injectionTest ConditionTest MethodTest ResultUnit
drying temperature80°C
Drying time - hot air dryer2.0 到 4.0hr
Suggested maximum moisture content0.20%
Processing (melt) temperature275 到 295°C
Melt Temperature, Optimum285°C
Mold temperature70 到 120°C
Mold Temperature, Optimum100°C
Maintain pressure50.0 到 100Mpa
Maintain pressureDrying Recommendedyes
Hold Pressure Time3.00s/mm
Maximum Screw Tangential Speed12m/min
Impact performanceTest ConditionTest MethodTest ResultUnit
Impact strength of simply supported beam without notch23°CISO 179/1eU75kJ/m²
flammabilityTest ConditionTest MethodTest ResultUnit
Burning rate1.00 mmISO 379528mm/min
UL flame retardant rating0.75 mmUL 94, IEC 60695-11-10, -20HB
UL flame retardant rating1.5 mmUL 94, IEC 60695-11-10, -20HB
FMVSS flammabilityFMVSS 302B
雾化 - G-value (condensate)ISO 64526.0E-4g
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.