PA66 Leona™ 14G25 ASAHI JAPAN
227
Unit Price:$3492 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 122.7MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Creep resistance Moderate heat resistance Thermal stability Fatigue resistance high strength High rigidity
- Application Areas:Electrical field Electronic field Engine hood parts component Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.32 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.9 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 干 | 旭化成方法 | 0.5/0.9 | % |
| Wear rate | 湿 | ASTM D-1044 | 12 | ×10-6kg/1000times |
| Shrinkage rate | TD | 内部方法 | 0.90 | % |
| MD | 内部方法 | 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 3 | % | |
| tensile strength | ASTM D638/ISO 527 | 180 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 96/120 | ||
| bending strength | ASTM D790/ISO 178 | 290 | kg·cm/cm(J/M)ft·lb/in | |
| ASTMD790 | 290 | Mpa | ||
| Bending stress | 23°C | ISO178 | 275 | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 3(6) | % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(-) | R scale |
| 干(湿) | ASTM D-785 | 96(74) | M Scale | |
| tensile strength | 干(湿) | ASTM D-638 | 180(110) | Mpa |
| Flexural strength | 干(湿) | ASTM D-790 | 290(175) | Mpa |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 8.1(4.7) | GPa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 105(160) | J/m |
| Tensile modulus | 23°C | ISO527-2 | 8200 | Mpa |
| Tensile strength | ASTMD638 | 180 | Mpa | |
| Tensile stress | Break,23°C | ISO527-2 | 190 | Mpa |
| elongation | Break | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | ASTMD790 | 8100 | Mpa | |
| 23°C | ISO178 | 7800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | 干 | UL 94 | HB | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 250 | °C |
| Linear expansion coefficient | 干 | ASTM D-696 | 3 | ×10-5/K |
| Thermal conductivity | 干 | 0.3 | W/(m.K) | |
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 260 | °C |
| Combustibility (rate) | UL94 | HB | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 3 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 260 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 260 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 250 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 245 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 3E-05 | cm/cm/°C |
| thermal conductivity | 0.30 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+15 | ohms | |
| IEC60093 | 1E+15 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| 23°C | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric strength | ASTMD149 | 29 | KV/mm | |
| IEC60243-1 | 29 | KV/mm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 425 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 68 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 96 | |
| R-Sale | ASTMD785 | 120 | ||
| M-Sale | ISO2039-2 | 96 | ||
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 1.9 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.