PA66 Leona™ 90G60 ASAHI JAPAN
124
- Unit Price:
- $3633 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 59.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity
- Application Areas:Automotive External Parts
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | 内部方法 | 0.50 | % |
| MD | 内部方法 | 0.20 | % | |
| 干 | 旭化成方法 | 0.2/0.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 干(湿) | ASTM D-785 | 95(88) | M Scale |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 16.0(12.9) | GPa |
| tensile strength | 干(湿) | ASTM D-638 | 190(148) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 2(3) | % |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 95(100) | J/m |
| Flexural strength | 干(湿) | ASTM D-790 | 300(234) | Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(117) | R scale |
| Tensile modulus | 23°C | ISO527-2 | 18200 | Mpa |
| Tensile strength | ASTMD638 | 190 | Mpa | |
| Tensile stress | Break,23°C | ISO527-2 | 189 | Mpa |
| elongation | Break | ASTMD638 | 2.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 2.0 | % |
| Bending modulus | ASTMD790 | 16000 | Mpa | |
| 23°C | ISO178 | 15800 | Mpa | |
| bending strength | ASTMD790 | 300 | Mpa | |
| Bending stress | 23°C | ISO178 | 324 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear expansion coefficient | 干 | ASTM D-696 | 2 | |
| Thermal conductivity | 干 | 0.3 | W/(m.K) | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 2E-05 | cm/cm/°C |
| specific heat | 1840 | J/kg/°C | ||
| thermal conductivity | 0.30 | W/m/K | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 230 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 225 | °C | |
| 1.82MPa,干 | ASTM D-648 | 225 | °C | |
| Specific heat capacity | 干 | 1840 | J/(kg.k) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+13 | ohms | |
| IEC60093 | 1E+13 | ohms | ||
| Dielectric strength | ASTMD149 | 28 | KV/mm | |
| IEC60243-1 | 28 | KV/mm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 475 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 56 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 95 | |
| R-Sale | ASTMD785 | 120 | ||
| M-Sale | ISO2039-2 | 95 | ||
| R-Sale | ISO2039-2 | 120 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 0.9 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.