Material Description

Technical Data Sheet

Material Description

Material Properties:Creep resistance Fatigue resistance high strength High rigidity
Application Areas:Electrical field Electronic field Industrial machinery Industrial applications Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	干	旭化成方法	0.5/0.9	%
Wear rate	湿	ASTM D-1044	12	×10-6kg/1000times
Shrinkage rate	TD	内部方法	0.90	%
Shrinkage rate	Shrinkage rate	MD	内部方法	0.50	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Flexural strength	干(湿)	ASTM D-790	290(175)	Mpa
Cantilever beam notch impact strength	干(湿)	ASTM D-256	105(160)	J/m
tensile strength	干(湿)	ASTM D-638	180(110)	Mpa
Fracture elongation rate	干(湿)	ASTM D-638	3(6)	%
Scratch resistance coefficient	干(湿)	ASTM D-790	8.1(4.7)	GPa
Rockwell hardness	干(湿)	ASTM D-785	96(74)	M Scale
Rockwell hardness	Rockwell hardness	干(湿)	ASTM D-785	120(-)	R scale
bending strength		ASTMD790	290	Mpa
Bending stress	23°C	ISO178	275	Mpa
Tensile modulus	23°C	ISO527-2	8200	Mpa
Tensile strength		ASTMD638	180	Mpa
Tensile stress	Break,23°C	ISO527-2	190	Mpa
elongation	Break	ASTMD638	3.0	%
Tensile strain	Break,23°C	ISO527-2	4.0	%
Bending modulus		ASTMD790	8100	Mpa
Bending modulus	Bending modulus	23°C	ISO178	7800	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	260	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	260	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	250	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	245	°C
Linear coefficient of thermal expansion	MD	ASTMD696	3E-05	cm/cm/°C
thermal conductivity			0.30	W/m/K
Hot deformation temperature	1.82MPa,干	ASTM D-648	250	°C
Thermal conductivity	干		0.3	W/(m.K)
Linear expansion coefficient	干	ASTM D-696	3	×10-5/K
Hot deformation temperature	0.46MPa,干	ASTM D-648	260	°C
Flame retardancy	干	UL 94	HB

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		ASTMD149	29	KV/mm
Dielectric strength	Dielectric strength		IEC60243-1	29	KV/mm
Leakage Trace Index	3.00mm	IEC60112	600	V
Surface resistivity		ASTMD257	1E+15	ohms
Surface resistivity	Surface resistivity		IEC60093	1E+15	ohms
Volume resistivity		ASTMD257	1E+15	ohms·cm
Volume resistivity	Volume resistivity	23°C	IEC60093	1E+15	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch		ISO179	68	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ASTMD785	96
	Rockwell hardness	R-Sale	ASTMD785	120
		Rockwell hardness	M-Sale	ISO2039-2	96
		Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	120

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating	0.75mm	UL94	HB

Basic performance	Test Condition	Test Method	Test Result	Unit
Moisture absorption rate	湿		1.9	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.