PA66 LNP™ LUBRICOMP™ RL-4530 SABIC INNOVATIVE US
95
- Unit Price:
- $3536 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan resist fatigue
- Application Areas:Electronic and electrical Automotive components Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 24hr | ASTM D955 | 1.0 到 3.0 | % |
| 流量 : 24hr | ISO 294-4 | 1.0 到 3.0 | % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.60 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.97 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 1 | ASTM D638 | 2690 | Mpa |
| -- | ISO 527-2/1 | 2960 | Mpa | |
| elongation | Yield 2 | ASTM D638 | 4.6 | % |
| Yield | ISO 527-2/5 | 4.8 | % | |
| Break 2 | ASTM D638 | 4.7 | % | |
| Break | ISO 527-2/5 | 4.7 | % | |
| Bending modulus | 50.0 mm Span 3 | ASTM D790 | 2260 | Mpa |
| -- 4 | ISO 178 | 2580 | Mpa | |
| Tensile strength | Yield 2 | ASTM D638 | 52.0 | Mpa |
| Yield | ISO 527-2/5 | 55.0 | Mpa | |
| Break 2 | ASTM D638 | 49.0 | Mpa | |
| Break | ISO 527-2/5 | 55.0 | Mpa | |
| Bending strength 3 | Yield, 50.0 mm Span | ASTM D790 | 73.0 | Mpa |
| Break, 50.0 mm Span | ASTM D790 | 73.0 | Mpa | |
| Friction coefficient 5 | Dynamic | ASTM D3702 | 0.22 | |
| Static | ASTM D3702 | 0.16 | ||
| Wear factor 5 | ASTM D3702 | 2.0E+6 | 10^-8 mm³/N·m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 201 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Bf | 221 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 59.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 66.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 9.1E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 9.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 9.6E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.15 到 0.25 | % | ||
| Processing (melt) temperature | 275 到 290 | °C | ||
| Mold temperature | 80 到 95 | °C | ||
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 265 到 275 | °C | ||
| Temperature in the middle of the barrel | 280 到 295 | °C | ||
| Temperature at the front of the material cylinder | 295 到 305 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 30 到 60 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 1.00 | J |
| -- | ISO 6603-2 | 0.00 | J | |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 380 | J/m |
| 23°C 6 | ISO 180/1U | 26 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.