PA66 Radiflam® A RV 300RKC RADIC ITALY
109
- Unit Price:
- $3985 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.35 | g/cm³ | |
| Shrinkage rate 3 | Across Flow | ISO 294-4 | 1.0 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Water absorption rate | Saturation, 23°C, 2.00 mm | ISO 62 | 7.0 | % |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 9500 | Mpa | |
| Tensile stress | Break | ISO 527-2/1A/5 | 180 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 3.9 | % |
| Bending modulus 4 | ISO 178 | 8500 | Mpa | |
| Bending stress 4 | ISO 178 | 275 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/Bf | 250 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/Af | 235 | °C | |
| Vicat softening temperature | ISO 306/B50 | 245 | °C | |
| Melting temperature 5 | ISO 11357-3 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity 6 | IEC 60093 | 1.0E+12 | ohms | |
| Volume resistivity 6 | IEC 60093 | 1.0E+15 | ohms·cm | |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying temperature - hot air dryer | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Dew Point - Hot Air Drying Machine | -20 | °C | ||
| Suggested maximum moisture content | 0.15 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Mold temperature | 80 到 100 | °C | ||
| Injection speed | 中等偏快 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 | kJ/m² |
| 23°C | ISO 179/1eA | 13 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 | kJ/m² |
| 23°C | ISO 179/1eU | 90 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 700 | °C |
| flammability | FMVSS 302 | 0 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.