PA66 Leona™ MR001 ASAHI JAPAN
109
- Unit Price:
- $3754 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High rigidity
- Application Areas:Engine parts Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.52 | ||
| Molding shrinkage rate | ASTM D955 | 1.0-1.1 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.5 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.0to1.1 | % |
| Wear rate | 湿 | ASTM D-1044 | 22 | |
| Shrinkage rate | 干 | 旭化成方法 | 1.0-1.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture elongation rate | 干(湿) | ASTM D-638 | 6(7) | % |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 5.6(3.3) | GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) | R scale |
| Flexural strength | 干(湿) | ASTM D-790 | 157(98) | Mpa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 34(39) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 85(60) | M Scale |
| tensile strength | 干(湿) | ASTM D-638 | 98(67) | Mpa |
| Rockwell hardness | ASTM D785 | R120 | ||
| Bending modulus | ASTM D790/ISO 178 | 5590(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 157(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| Tensile stress | Break,23°C | ISO527-2 | 93.0 | Mpa |
| elongation | Break | ASTMD638 | 6.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 5.5 | % |
| Bending modulus | ASTMD790 | 5600 | Mpa | |
| 23°C | ISO178 | 5800 | Mpa | |
| bending strength | ASTMD790 | 157 | Mpa | |
| Bending stress | 23°C | ISO178 | 150 | Mpa |
| Tensile modulus | 23°C | ISO527-2 | 5900 | Mpa |
| Tensile strength | ASTMD638 | 98.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 240 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 229 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 160 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 118 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 6E-05 | cm/cm/°C |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 240 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 6 | mm/mm.℃ | |
| 干 | ASTM D-696 | 6 | ||
| Hot deformation temperature | 0.46MPa,干 | ASTM D-648 | 240 | °C |
| Flame retardancy | 干 | UL 94 | HB | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 160 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+13 | ohms | |
| IEC60093 | 1E+13 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+14 | ohms·cm | |
| 23°C | IEC60093 | 1E+14 | ohms·cm | |
| Dielectric strength | ASTMD149 | 22 | KV/mm | |
| IEC60243-1 | 22 | KV/mm | ||
| Arc resistance | ASTM D495/IEC 60112 | 87 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 62 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 85 | |
| R-Sale | ASTMD785 | 120 | ||
| M-Sale | ISO2039-2 | 85 | ||
| R-Sale | ISO2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture absorption rate | 湿 | 1.5 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.