PA66 Zytel® 408L DUPONT USA

102

Unit Price:
$2519 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance
Application Areas:Industrial machinery Industrial applications Non specific food applica
Color:--
Grade:Special level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Saturation,23°C,2.00mm	ISO62	7.0	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	2.2	%
Shrinkage rate	TD	ISO294-4	1.5	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.5	%
MediumDensity			0.950	g/cm³
Top out temperature			190	°C
SpecificHeatCapacity of Melt			2600	J/kg/°C
ThermalConductivityofMelt			0.16	W/m/K
Density/specific gravity		ISO1183	1.09	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Nominal tensile fracture strain		ISO527-2	35	%
Tensile creep modulus	1000hr	ISO899-1	--	Mpa
Tensile stress	Yield	ISO527-2	61.0	Mpa
Tensile strain	Yield	ISO527-2	6.0	%
Tensile modulus		ISO527-2	2200	Mpa
TensileCreepModule	1hr	ISO899-1	--	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	155	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	66.0	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.3E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.3E-04	cm/cm/°C
Vicat softening temperature		ISO306/B50	210	°C
Melting temperature 2		ISO11357-3	263	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	34	KV/mm
Dissipation factor	100Hz	IEC60250	0.020
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.020
Surface resistivity		IEC60093	--	ohms
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Relative permittivity	100Hz	IEC60250	3.20
Relative permittivity	Relative permittivity	1MHz	IEC60250	2.90
Leakage Trace Index		IEC60112	600	V

film	Test Condition	Test Method	Test Result	Unit
Tensile strain MD	Yield	ISO527-3	6.0	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO179/1eA	15	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	15	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.75mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	19	%
FMVSS flammability		FMVSS302	B
Burning rate 3	1.00mm	ISO3795	<100	mm/min

Supplementary Information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	35.0	µgC/g
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.