PA6 LNP™ THERMOCOMP™ PX13012-BKNAT SABIC INNOVATIVE NETHERLANDS
54
- Unit Price:
- $2840 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low Specific Gravity Filler: Mineral filler
- Application Areas:Automotive body panels Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flow direction: 24 hours | ISO294-4 | 0.55 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.23 | % |
| Flow 1 | 内部方法 | 0.70 | % | |
| Flow: 24 hours | ASTMD955 | 0.55 | % | |
| Lateral flow: 24 hours | ASTMD955 | 0.65 | % | |
| Vertical flow direction: 24 hours | ISO294-4 | 0.65 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --2 | ASTMD638 | 10400 | Mpa | |
| Surrender 3 | ASTMD638 | 68.0 | Mpa | |
| crack | ISO527-2/5 | 75.0 | Mpa | |
| Fracture 4 | ASTMD638 | 1.2 | % | |
| crack | ISO527-2/5 | 1.1 | % | |
| 50.0mm span 5 | ASTMD790 | 11800 | Mpa | |
| --6 | ISO178 | 12000 | Mpa | |
| --7 | ISO178 | 105 | Mpa | |
| Fracture, 50.0mm span 8 | ASTMD790 | 119 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 203 | °C | |
| 0.45MPa, unannealed, 64.0mm span 11 | ISO75-2/Bf | 203 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 137 | °C | |
| 1.8MPa, unannealed, 64.0mm span 12 | ISO75-2/Af | 160 | °C | |
| BallPressure Test | 165°C | IEC60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 3.3E-05 | cm/cm/°C | |
| Flow: -30 to 80 ° C | ISO11359-2 | 3.9E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 4.4E-05 | cm/cm/°C | |
| Horizontal: -30 to 80 ° C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| thermal conductivity | --13 | ISO22007-2 | 1.2 | W/m/K |
| --14 | ISO22007-2 | 5.5 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 4E+14 | ohms | |
| Dielectric strength | 1.60mm,inOil | ASTMD149 | 7.2 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Leakage Trace Index | IEC60112 | 600 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C | ASTMD256 | 15 | J/m | |
| 23°C9 | ISO180/1A | 3.0 | kJ/m² | |
| 23°C | ASTMD4812 | 150 | J/m | |
| 23°C10 | ISO180/1U | 9.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL94 | V-0 | |
| Burning wire flammability index | 0.800mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.800mm | IEC60695-2-13 | 750 | °C |
| 1.60mm | IEC60695-2-13 | 775 | °C | |
| 3.00mm | IEC60695-2-13 | 800 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.