| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Molten Volume Flow Rate (MVR) | 275°C/5.0 kg | ISO 1133 | 45.0 | cm3/10min |
| Shrinkage rate | Across Flow : 23°C, 72hr | ISO 2577 | 0.80 到 1.0 | % |
| Shrinkage rate | 流量 : 23°C, 72hr | ISO 2577 | 0.30 到 0.50 | % |
| Stickiness number | 96% H2SO4 | ISO 307 | 145 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-2/1 | 9500 | Mpa |
| Tensile stress | Break | ISO 527-2/5 | 180 | Mpa |
| Tensile strain | Break | ISO 527-2/5 | 3.5 | % |
| Bending modulus 3 | | ISO 178 | 8500 | Mpa |
| Bending stress 3 | | ISO 178 | 270 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 220 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 200 | °C |
| Vicat softening temperature | | ISO 306/B50 | 215 | °C |
| Melting temperature | | ISO 11357-3 | 221 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 1.0E+13 | ohms |
| Volume resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
| Leakage Trace Index | Solution A | IEC 60112 | 500 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 75 到 85 | °C |
| drying time | | | 2.0 到 4.0 | hr |
| Processing (melt) temperature | | | 240 到 270 | °C |
| Mold temperature | | | 90 到 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO 180/1U | 80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 122 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning rate | | FMVSS 302 | < 100 | mm/min |
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
| Burning wire flammability index | 1.0 to 3.0 mm | IEC 60695-2-12 | 650 | °C |
| ISO 9660 | | ISO 1874 | PA6,ML,14-090,GF30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.