PA6 Ultramid® HPN9233G BK5830 BASF KOREA
111
- Unit Price:
- $3243 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant High impact resistance
- Application Areas:film Electrical enclosure
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.30 | % | |
| Water absorption rate | 24hr | ASTMD570 | 1.1 | % |
| 23°C,24hr | ISO62 | 1.1 | % | |
| Saturation | ASTMD570 | 6.4 | % | |
| Saturation,23°C | ISO62 | 6.4 | % | |
| Equilibrium,50%RH | ASTMD570 | 1.8 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 1.8 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break,23°C | ASTMD638 | 175 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 175 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ASTMD790 | 9380 | Mpa |
| 23°C | ISO178 | 8400 | Mpa | |
| bending strength | 23°C | ASTMD790 | 265 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | 6.0mm | UL746 | 140 | °C |
| Evolution Calendar intelligent importer | 0.71mm | UL746 | 115 | °C |
| 1.5mm | UL746 | 115 | °C | |
| 3.0mm | UL746 | 120 | °C | |
| 6.0mm | UL746 | 120 | °C | |
| RTIStr | 0.71mm | UL746 | 140 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| 6.0mm | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 174 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 208 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 54.0 | °C | |
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 3.8E-05 | cm/cm/°C |
| RTIElec | 0.71mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+13 | ohms·cm | |
| Dielectric strength 2 | 1.50mm | ASTMD149 | 22 | KV/mm |
| VolumeResistivity | 1.50mm | ASTMD257 | >1.0E+13 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling impact resistance | 23°C | 内部方法 | 4.61 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 6.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.