PA6 Durethan® BKV315ZH2.0 901510 LANXESS GERMANY

128

Unit Price:
$3016 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
45.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		ISO60	0.70	g/cm³
Shrinkage rate	TD:280°C,2.00mm2	ISO294-4	0.60	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO294-4	0.10	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO294-4	0.90	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO294-4	0.20	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2/1	5300	Mpa
Tensile stress	Break,23°C	ISO527-2/5	105	Mpa
Tensile strain	Break,23°C	ISO527-2/5	5.0	%
Bending modulus 4	23°C	ISO178/A	4800	Mpa
Bending stress 4	3.5%Strain	ISO178/A	150	Mpa
	Bending stress 4	23°C	ISO178	165	Mpa
	Bending stress 4	Bending stress 4	FlexuralStrainatFlexuralStrength5(23°C)		5.5	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	210	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	175	°C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	58.0	°C
Melting temperature 5		ISO11357-3	221	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	1.3E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index	SolutionA	IEC60112	375	V

film	Test Condition	Test Method	Test Result	Unit
Membrane puncture strength	--6	ISO6603-2	2.50	J
Membrane puncture strength	Membrane puncture strength	--7	ISO6603-2	4.90	J
Membrane piercing force	--6	ISO6603-2	630	N
Membrane piercing force	Membrane piercing force	--7	ISO6603-2	1200	N

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	85	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	80	kJ/m²
Unscented Izod impact strength	-30°C	ISO180/1U	70	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	65	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	140	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
BurningBehavior9		ISO3795	passed

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO1874	PA6-HI,BHR,14-050,GF15

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.