PA6 LNP™ KONDUIT™ PX11313-WH5G004 SABIC INNOVATIVE US
140
- Unit Price:
- $6926 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 56MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non chloro non bromine fl heat conduction
- Application Areas:Electronic and Electrical Electronic display Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 24hr | ASTM D955 | 0.42 | % |
| Across Flow : 24hr | ASTM D955 | 0.58 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.040 | % |
| 24 hr, 23°C 2 | ISO 62 | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break 4 | ASTM D638 | 98.0 | Mpa |
| Break | ISO 527-2/5 | 108 | Mpa | |
| Tensile modulus | -- 3 | ASTM D638 | 13300 | Mpa |
| -- | ISO 527-2/1 | 13300 | Mpa | |
| elongation | Break 4 | ASTM D638 | 1.3 | % |
| Break | ISO 527-2/5 | 1.3 | % | |
| Bending modulus | 50.0 mm Span 5 | ASTM D790 | 12500 | Mpa |
| -- 6 | ISO 178 | 13000 | Mpa | |
| Bending stress | -- 6, 7 | ISO 178 | 186 | Mpa |
| Yield, 50.0 mm Span 5 | ASTM D790 | 167 | Mpa | |
| Break, 50.0 mm Span 5 | ASTM D790 | 176 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | Flow : 40 to 120°C | ASTM E831 | 4.1E-5 | cm/cm/°C |
| Across Flow : 40 to 120°C | ASTM E831 | 8.5E-5 | cm/cm/°C | |
| thermal conductivity | -- 9 | ASTM E1461 | 1.4 | W/m/K |
| -- 10 | ASTM E1461 | 1.8 | W/m/K | |
| -- 11 | ISO 22007-2 | 0.90 | W/m/K | |
| -- 12 | ISO 22007-2 | 1.9 | W/m/K | |
| RTI | UL 746 | 120 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 227 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Bf | 228 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 215 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 208 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1.10 GHz | ASTM ES7-83 | 9.9E-3 | |
| Surface resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Dielectric constant | 1.10 GHz | ASTM ES7-83 | 4.84 | |
| Dielectric strength | 1.00 mm, in Oil | ASTM D149 | > 10 | KV/mm |
| Leakage Trace Index | IEC 60112 | 600 | V | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | ||
| High arc combustion index (HAI) 13 | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 260 到 275 | °C | ||
| Temperature in the middle of the barrel | 270 到 290 | °C | ||
| Temperature at the front of the material cylinder | 270 到 290 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 20 到 60 | rpm | ||
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.15 到 0.25 | % | ||
| Processing (melt) temperature | 270 到 295 | °C | ||
| Mold temperature | 85 到 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 330 | J/m |
| 23°C 8 | ISO 180/1U | 23 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.0 to 3.0 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 750 | °C |
| 3.0 mm | IEC 60695-2-13 | 800 | °C | |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.