PA6 Akulon® F130-C DSM HOLAND
129
Unit Price:$3350 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 64MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity
- Application Areas:film
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Stickiness number | ISO 307 | 196 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| friction coefficient | Dynamic | ISO 8295 | 1.0 | |
| Static | ISO 8295 | 1.2 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| Specific Heat Capacity | 1550 | J/kg/°C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 50 | µm | ||
| Tensile modulus 2 | 内部方法 | 455 | Mpa | |
| Tensile stress - MD | Yield | ISO 527-3 | 31.0 | Mpa |
| Break | ISO 527-3 | 82.0 | Mpa | |
| Elongation - MD | Break | ISO 527-3 | 350 | % |
| Trouser Tear - Parallel | ISO 6383-1 | 32.0 | ||
| Water vapor permeability | 23°C, 85% RH | DIS 15106-1/-3 | 35 | g/m²/24 hr |
| Oxygen transmission rate | 0% RH : 23°C | ASTM D256A | 26 | cm³/m²/bar/24 hr |
| 85% RH : 23°C | ASTM D256A | 38 | cm³/m²/bar/24 hr |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C | 内部方法 | 810000 | mPa·s |
| Average Specific Heat Capacity | 20 to 150°C | 2250 | J/kg/°C | |
| Puncture Resistance | 内部方法 | 13.0 | J/cm | |
| RSV - Formic Acid, 1g/100ml | 内部方法 | 3.03 |
| squeeze | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Temperature in Zone 1 of the material cylinder | 270 | °C | ||
| Temperature in Zone 2 of the material cylinder | 270 | °C | ||
| Temperature in Zone 3 of the material cylinder | 270 | °C | ||
| Temperature in Zone 4 of the material cylinder | 270 | °C | ||
| Oral mold temperature | 270 | °C | ||
| Traction roller | 110 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Clarity | 内部方法 | 83 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.