PA6 Durethan® BKV330 H2.0 LANXESS GERMANY

127

Unit Price:
$2835 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
46MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Flame retardant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Apparent density		ISO60	0.70	g/cm³
Shrinkage rate	TD:280°C,2.00mm2	ISO294-4	0.70	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO294-4	0.070	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO294-4	0.35	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO294-4	0.060	%
Water absorption rate	Saturation,23°C	ISO62	6.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.3	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2/1	9800	Mpa
Tensile stress	Break,23°C	ISO527-2/5	170	Mpa
Tensile strain	Break,23°C	ISO527-2/5	3.0	%
Bending modulus 4	23°C	ISO178/A	8300	Mpa
Bending stress 4	3.5%Strain	ISO178/A	245	Mpa
	Bending stress 4	23°C	ISO178	260	Mpa
	Bending stress 4	Bending stress 4	FlexuralStrainatFlexuralStrength5(23°C)		4.5	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	8.0MPa,Unannealed	ISO75-2/C	90.0	°C
Vicat softening temperature	--	ISO306/B50	>200	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	>200	°C
Melting temperature 5		ISO11357-3	222	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	215	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	200	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative permittivity	23°C,1MHz	IEC60250	3.90
Dissipation factor	23°C,100Hz	IEC60250	0.019
Leakage Trace Index	SolutionA	IEC60112	450	V
Surface resistivity		IEC60093	1E+13	ohms
Volume resistivity	23°C	IEC60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC60243-1	32	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	4.50

film	Test Condition	Test Method	Test Result	Unit
Membrane puncture strength	--6	ISO6603-2	2.80	J
Membrane puncture strength	Membrane puncture strength	--7	ISO6603-2	3.40	J
Membrane piercing force	--6	ISO6603-2	791	N
Membrane piercing force	Membrane piercing force	--7	ISO6603-2	883	N

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	80	kJ/m²
Unscented Izod impact strength	-30°C	ISO180/1U	75	kJ/m²
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	75	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	195	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	HB
Burning wire flammability index	2.0mm	IEC60695-2-12	700	°C
Extreme Oxygen Index 9		ISO4589-2	23	%
BurningBehavior10		ISO3795	passed

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut		ISO1874	PA6,GHR,14-100,GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.