PA6 UBE 1015GNKF BK UBE JAPAN
214
- Unit Price:
- $2302 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 54.7MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 30% Filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | 内部方法 | 0.70 | % |
| MD | 内部方法 | 0.20 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | 内部方法 | 1.8 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 9900 | Mpa | |
| Tensile stress | Break | ISO527-2 | 190 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.3 | % |
| Bending modulus | ISO178 | 9800 | Mpa | |
| Bending stress | ISO178 | 290 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 12 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.