PA6 Amilan® CM1026 TORAY JAPAN
147
Unit Price:$2835 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Medium viscosity
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.8 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber wear amount | 1000g,CS-17 | ASTM D-1044 | 无水｜3-4 | mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- | mg/1000次 | |
| Shrinkage rate | MD：3.00mm4 | % | 0.80到1.6 | -- |
| Water absorption rate | 23°C,24hr | % | 1.8 | -- |
| Saturation,23°C | % | 11 | -- | |
| Shrinkage rate | MD：1.00mm3 | % | 0.40到0.90 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | -40°C | MPa | 110 | |
| 23°C | MPa | 80.0 | 35.0 | |
| Flexural strength | 80℃ | ASTM D-790 | 无水｜430 | kg/cm2 |
| 80℃ | ASTM D-790 | 3.5%水｜250 | kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜119 | R-标度 |
| Tensile stress | 80°C | MPa | 25.0 | 20.0 |
| Tensile strain | Yield,23°C | % | 1.5 | -- |
| Break,23°C | % | 50 | ||
| Rockwell hardness | 80℃ | ASTM D-785 | 无水｜80 | R-标度 |
| 80℃ | ASTM D-785 | 3.5%水｜- | R-标度 | |
| compressive strength | 23℃ | ASTM D-695 | 无水｜820 | kg/cm2 |
| 23℃ | ASTM D-695 | 3.5%水｜650 | kg/cm2 | |
| Tensile yield strength | 23℃ | ASTM D-638 | 无水｜760 | kg/cm2 |
| 23℃ | ASTM D-638 | 3.5%水｜350 | kg/cm2 | |
| Flexural strength | -40℃ | ASTM D-790 | 无水｜1400 | kg/cm2 |
| -40℃ | ASTM D-790 | 3.5%水｜1300 | kg/cm2 | |
| Tensile yield strength | -40℃ | ASTM D-638 | 无水｜1130 | kg/cm2 |
| -40℃ | ASTM D-638 | 3.5%水｜1000 | kg/cm2 | |
| Bending modulus | -40°C | MPa | 3800 | 3600 |
| 23°C | MPa | 2600 | ||
| 80°C | MPa | 700 | 300 | |
| Bending stress | -40°C | MPa | 135 | |
| 23°C | MPa | 110 | 40.0 | |
| 80°C | MPa | 40.0 | 25.0 | |
| Compressive stress | 23°C | MPa | 80.0 | -- |
| shear strength | 23°C | MPa | 70.0 | 65.0 |
| Taber abraser | 1000Cycles | mg | 3.00到4.00 | -- |
| Friction coefficient vs. Metal5 | 0.15到0.20 | -- | ||
| Shear strength | 23℃ | ASTM D-792 | 无水｜720 | kg/cm2 |
| elongation at break | 23℃ | ASTM D-638 | 3.5%水｜<200 | % |
| Flexural modulus | -40℃ | ASTM D-790 | 无水｜39000 | kg/cm2 |
| -40℃ | ASTM D-790 | 3.5%水｜37000 | kg/cm2 | |
| Shear strength | 23℃ | ASTM D-792 | 3.5%水｜650 | kg/cm2 |
| Tensile yield strength | 80℃ | ASTM D-638 | 无水｜270 | kg/cm2 |
| 80℃ | ASTM D-638 | 3.5%水｜200 | kg/cm2 | |
| Flexural modulus | 23℃ | ASTM D-790 | 无水｜25000 | kg/cm2 |
| 23℃ | ASTM D-790 | 3.5%水｜8000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 无水｜7000 | kg/cm2 | |
| 80℃ | ASTM D-790 | 3.5%水｜3000 | kg/cm2 | |
| elongation at break | 23℃ | ASTM D-638 | 无水｜<200 | % |
| Rockwell hardness | ASTM D785 | 80 | ||
| 23℃ | ASTM D-785 | 3.5%水｜88 | R-标度 | |
| Flexural strength | 23℃ | ASTM D-790 | 无水｜1000 | kg/cm2 |
| 23℃ | ASTM D-790 | 3.5%水｜400 | kg/cm2 | |
| Tensile fracture strength | 23℃ | ASTM D-638 | 无水｜800 | kg/cm2 |
| 23℃ | ASTM D-638 | 3.5%水｜520 | kg/cm2 | |
| IZOD impact strength | 23℃，Unnotched1/8 | ASTM D-256 | 无水｜6.5 | kg.cm/cm |
| 23℃，Unnotched1/8 | ASTM D-256 | 3.5%水｜<50 | kg.cm/cm | |
| 23℃，Unnotched1/8 | 无水｜无裂断 | kg·cm/cm2 | ||
| 23℃，Unnotched1/8 | 3.5%水｜- | kg·cm/cm2 | ||
| -40℃，Unnotched1/2 | ASTM D-256 | 无水｜4.5 | kg.cm/cm | |
| -40℃，Unnotched1/2 | ASTM D-256 | 3.5%水｜- | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 182 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 | -- |
| specific heat | J/kg/°C | 1900 | -- | |
| thermal conductivity | W/m/K | 0.25 | -- | |
| melting point | 225 | ℃（℉） | ||
| UL-94 flame retardant grade | UL 94 | 无水｜HB(1/16") | ||
| UL 94 | 3.5%水｜- | |||
| heat deflection temperature | 4.6kg/cm2 | ASTM D-648 | 无水｜182 | °C |
| 4.6kg/cm2 | ASTM D-648 | 3.5%水｜- | °C | |
| specific heat | 无水｜0.46 | Cal/g·℃ | ||
| 3.5%水｜- | Cal/g·℃ | |||
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜8 | ×10-5cm/cm/℃ | |
| ASTM D-696 | 3.5%水｜- | ×10-5cm/cm/℃ | ||
| thermal conductivity | 无水｜0.18 | Kcal/m·hr·℃ | ||
| 3.5%水｜- | Kcal/m·hr·℃ | |||
| melting point | 差示扫描测热计DSC | 无水｜225 | °C | |
| 差示扫描测热计DSC | 3.5%水｜- | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10^11~12 | Ω.cm | |
| ASTM D-257 | 无水｜1013-1014 | Ω.cm | ||
| ASTM D-257 | 3.5%水｜1011-1012 | Ω.cm | ||
| ohms·cm | 1.0E+13到1.0E+14 | 1.0E+11到1.0E+12 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | 无断裂 | -- | |
| 23°C | 无断裂 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | 119 | ||
| R-Sale,80°C | 80 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | HB | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃，24hr | ASTM D-570 | 无水｜1.8 | % |
| 23℃，24hr | ASTM D-570 | 3.5%水｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.