PA6 Grilon® BG-30S EMS-CHEMIE SWITZERLAND
219
- Unit Price:
- $3378 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High impact resistance
- Application Areas:Electrical applications Home appliance components Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | 100000000000000 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 40 | KV/mm | |
| Compared to the leakage trace index | IEC 60112 | -- | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | -30℃ -30°C | ISO 179/1eA | 8 | kJ/m² |
| 23℃ 23°C | ISO 179/1eA | 11 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30℃ -30°C | ISO 179/1eU | 65 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | 75 | kJ/m² |
| Physical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ISO 1183 | 1.35 | g/cm³ | |
| Shrinkage rate | TD Across Flow | ISO 294-4 | 0.8 | % |
| MD Flow | ISO 294-4 | 0.1 | % | |
| Water absorption rate | Saturation，23℃ Saturation, 73°F | ISO 62 | 7 | % |
| Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO 2039-1 | 210 | Mpa | |
| Tensile modulus | ISO 527-2 | 9500 | Mpa | |
| Tensile strength | Break Break | ISO 527-2 | 185 | Mpa |
| Tensile strain | Break Break | ISO 527-2 | 5 | % |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.8 mm 0.8 mm | IEC 60695-11-10, -20 | HB |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 205 | °C |
| 8.0 MPa，Unannealed 1160 psi, Unannealed | ISO 75-2/C | 135 | °C | |
| Continuous use temperature | -- -- 3 3 | ISO 2578 | 90.0 到 110 | °C |
| -- -- 4 4 | 内部方法 | 160 | °C | |
| Melting temperature | ISO 11357-3 | 222 | °C | |
| Linear coefficient of thermal expansion CLTE | MD Flow | ISO 11359-2 | 0.000020 | 1/℃ |
| TD Transverse | ISO 11359-2 | 0.00011 | 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.