PA6 Ultramid® 8253HS BK102 BASF GERMANY
115
- Unit Price:
- $3800 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 57MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability high strength Oil resistant
- Application Areas:Helmet Gear Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 1.2 | % | |
| Water absorption rate | 24hr | ASTMD570 | 1.5 | % |
| 23°C,24hr | ISO62 | 1.5 | % | |
| Saturation | ASTMD570 | 8.1 | % | |
| Saturation,23°C | ISO62 | 8.1 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.3 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 2400 | Mpa |
| elongation | Break,23°C | ASTMD638 | >100 | % |
| Yield,23°C | ASTMD638 | 4.0 | % | |
| Bending modulus | 23°C | ASTMD790 | 2270 | Mpa |
| 23°C | ISO178 | 1900 | Mpa | |
| bending strength | 23°C | ASTMD790 | 85.0 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 60.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 4.0 | % |
| Bending stress | 23°C | ISO178 | 65.0 | Mpa |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 40 | % |
| Tensile strength | Yield,23°C | ASTMD638 | 65.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 60.0 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 55.0 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| RTIElec | 0.71mm | UL746 | 105 | °C |
| 0.75mm | UL746 | 105 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| Evolution Calendar intelligent importer | 0.71mm | UL746 | 95.0 | °C |
| 0.75mm | UL746 | 95.0 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| RTIStr | 0.71mm | UL746 | 95.0 | °C |
| 0.75mm | UL746 | 95.0 | °C | |
| 1.5mm | UL746 | 105 | °C | |
| 3.0mm | UL746 | 105 | °C | |
| 6.0mm | UL746 | 105 | °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 9.9E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak | |
| Falling impact resistance | 23°C | 内部方法 | 271 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 82 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB | ||
| 6.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.