PA6 Ultramid® 8202C BASF GERMANY

163

Unit Price:$3099 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 128MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability high strength Oil resistant
Application Areas:Helmet Engine parts Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ASTMD792	1.13	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.13	g/cm³
Shrinkage rate	MD：3.18mm		0.90	%
Water absorption rate	24hr	ASTMD570	1.6	%
	Water absorption rate	23°C,24hr	ISO62	1.6	%
		Water absorption rate	Saturation	ASTMD570	9.3	%
			Water absorption rate	Saturation,23°C	ISO62	9.3	%
				Water absorption rate	Equilibrium,50%RH	ASTMD570	2.6	%
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.6	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-40°C	ISO527-2	4090	Mpa
Tensile modulus	Tensile modulus	23°C	ISO527-2	3700	Mpa
Tensile stress	Yield,120°C	ISO527-2	30.0	Mpa
Tensile stress	Tensile stress	Yield,150°C	ISO527-2	25.0	Mpa
Tensile strength	Break,-40°C	ASTMD638	130	Mpa
	Tensile strength	Break,23°C	ASTMD638	90.0	Mpa
		Tensile strength	Break,80°C	ASTMD638	35.0	Mpa
		Tensile strength	Tensile strength	Break,121°C	ASTMD638	25.0	Mpa
elongation	Yield,-40°C	ASTMD638	3.0	%
	elongation	Yield,23°C	ASTMD638	4.0	%
		elongation	Yield,80°C	ASTMD638	25	%
		elongation	elongation	Yield,121°C	ASTMD638	27	%
Bending modulus	23°C	ASTMD790	3170	Mpa
	Bending modulus	65°C	ASTMD790	600	Mpa
		Bending modulus	90°C	ASTMD790	440	Mpa
			Bending modulus	121°C	ASTMD790	385	Mpa
			Bending modulus	Bending modulus	23°C	ISO178	2800	Mpa
bending strength	-40°C	ASTMD790	183	Mpa
	bending strength	23°C	ASTMD790	110	Mpa
		bending strength	65°C	ASTMD790	30.0	Mpa
		bending strength	bending strength	121°C	ASTMD790	21.0	Mpa
Bending stress	23°C	ISO178	95.0	Mpa
Tensile modulus	80°C	ISO527-2	750	Mpa
	Tensile modulus	120°C	ISO527-2	550	Mpa
	Tensile modulus	Tensile modulus	150°C	ISO527-2	445	Mpa
Tensile strength	Yield,-40°C	ASTMD638	137	Mpa
	Tensile strength	Yield,23°C	ASTMD638	90.0	Mpa
		Tensile strength	Yield,80°C	ASTMD638	40.0	Mpa
		Tensile strength	Tensile strength	Yield,121°C	ASTMD638	30.0	Mpa
Tensile stress	Yield,-40°C	ISO527-2	137	Mpa
	Tensile stress	Yield,23°C	ISO527-2	88.0	Mpa
	Tensile stress	Tensile stress	Yield,80°C	ISO527-2	40.0	Mpa
Tensile strain	Yield,23°C	ISO527-2	4.0	%
elongation	Break,-40°C	ASTMD638	5.0	%
	elongation	Break,23°C	ASTMD638	12	%
		elongation	Break,80°C	ASTMD638	>100	%
		elongation	elongation	Break,121°C	ASTMD638	>100	%
Nominal tensile fracture strain	-40°C	ISO527-2	5.0	%
	Nominal tensile fracture strain	23°C	ISO527-2	7.0	%
		Nominal tensile fracture strain	80°C	ISO527-2	>100	%
		Nominal tensile fracture strain	Nominal tensile fracture strain	120°C	ISO527-2	>100	%
Bending modulus	-40°C	ASTMD790	3370	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Evolution Calendar intelligent importer	6.0mm	UL746	105	°C
RTIStr	0.71mm	UL746	95.0	°C
	RTIStr	1.5mm	UL746	105	°C
		RTIStr	3.0mm	UL746	105	°C
		RTIStr	RTIStr	6.0mm	UL746	105	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	190	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	165	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	75.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	65.0	°C
Peak melting temperature		ASTMD3418	220	°C
Melting temperature (DSC)		ISO3146	220	°C
Linear coefficient of thermal expansion	MD	ASTME831	8.1E-05	cm/cm/°C
RTIElec	0.71mm	UL746	130	°C
	RTIElec	1.5mm	UL746	130	°C
		RTIElec	3.0mm	UL746	130	°C
		RTIElec	RTIElec	6.0mm	UL746	130	°C
Evolution Calendar intelligent importer	0.71mm	UL746	95.0	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	105	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	105	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
VolumeResistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Volume resistivity		IEC60093	>1.0E+13	ohms·cm
Dielectric strength 2	1.50mm	ASTMD149	30	KV/mm
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179	3.5	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179	NoBreak
Impact strength of cantilever beam gap	-40°C	ASTMD256	32	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTMD256	48	J/m
Falling impact resistance	23°C	内部方法	122	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	120

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.71mm	UL94	V-2
	UL flame retardant rating	1.5mm	UL94	V-2
		UL flame retardant rating	3.0mm	UL94	V-2
		UL flame retardant rating	UL flame retardant rating	6.0mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.