PA6 Ultramid® B3EG5 BASF GERMANY
127
- Unit Price:
- $2505 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 170.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1320 | ||
| Molding shrinkage rate | ASTM D955 | 0.35 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 55 （cm3/10min 275℃/5kg ) | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 6.8-7.4 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 23℃ | % | 0,20到1,0 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break,23℃ | MPa | 95.17到284.83 | |
| Tensile strain | Break,23℃ | % | 2,5到3,0 | |
| Tensile modulus | 23℃ | MPa | 0.01,0.01E0.05到0.01,0.04E0.05 | |
| ASTM D638/ISO 527 | 8000 | kg/cm²(MPa)[Lb/in²] | ||
| Bending modulus | ASTM D790/ISO 178 | 7400 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 2020 | kg/cm²(MPa)[Lb/in²] | |
| Tensile creep modulus | 1000h，湿 | 3000 | Mpa | |
| Bending modulus | 干/湿 | 7400/4200 | Mpa | |
| Tensile modulus of elasticity | 干/湿 | 8000/5500 | Mpa | |
| Yield elongation (V=50mm/min) | 干/湿 | 3.5/8.5 | % | |
| Ball pressure hardness | 干/湿 | 210/140 | Mpa | |
| Kabi impact strength | 30℃，干 | 75 | KJ/m | |
| Izo notch impact strength | +23℃，干/湿 | 12/17 | KJ/m | |
| Elongation at break (V=50mm/min) | 干/湿 | 3.5/8.5 | % | |
| bending strength | 干/湿 | 220/150 | Mpa | |
| elongation | ≤0.5%, +23℃，湿 | 3000 | Mpa | |
| Kabi impact strength | 干/湿 | 80/105 | KJ/m | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 160/105 | Mpa | |
| Fracture stress (V=50mm/min) | 干/湿 | 160/105 | Mpa | |
| Kapi notch impact strength | 30℃，干/湿 | 10 | KJ/m | |
| +23℃，干/湿 | 12/25 | KJ/m | ||
| Charpy impact strength | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 75 | kg·cm/cm(J/M)ft·lb/in | ||
| IZOD notch impact strength | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 3.5 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | °C | 239到261 | |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 210(1.80MPa) | ℃（℉） | |
| melting point | 220 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.2-0.25 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa负荷，Dry | 220 | °C | |
| Temperature index | 在20000h/5000h，后拉伸强度下降50%时 | 120/150 | °C | |
| Specific heat capacity | Dry | 1.5 | J/(g.K) | |
| Linear coefficient of thermal expansion | 23-80℃Dry | 2-2.5/6-7 | ||
| Hot deformation temperature | 1.8MPa负荷，Dry | 210 | °C | |
| Thermal conductivity | Dry | 0.26 | W/(m.K) | |
| Maximum operating temperature | 200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1MHz，干/湿 | 3.8/7 | ||
| Surface resistance | 干/湿 | 10 | Ω | |
| Dielectric strength | K20/P50，干/湿 | 80/70 | KV/mm | |
| Volume resistance | 干/湿 | 10 | Ω.cm | |
| Loss angle | 1MHz，干/湿 | 0.025/0.24 | ||
| Dielectric constant | ASTM D150/IEC 60250 | 3.8 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1E 13 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 10.679到17.642 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact and destructive energy | +23℃干/湿 | 10/30 | J | |
| Relative arc track index CT1 | 干/湿 | 干/湿 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.