PA6 Amilan® CM1056 TORAY JAPAN
127
- Unit Price:
- $2709 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.09 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | % | 1.7 | -- |
| Saturation,23°C | % | 8.0 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | -40°C | MPa | 105 | 95.0 |
| 23°C | MPa | 60.0 | 35.0 | |
| 80°C | MPa | 25.0 | 20.0 | |
| Tensile strain | Break,-40°C | % | 3.5 | 1.0 |
| Break,23°C | % | 50 | ||
| Break,80°C | % | 50 | ||
| Tensile yield strength | 80℃ | ASTM D-638 | Dry｜25 | Mpa |
| 80℃ | ASTM D-638 | 3.0%Water｜20 | Mpa | |
| 23℃ | ASTM D-638 | Dry｜60 | Mpa | |
| 23℃ | ASTM D-638 | 3.0%Water｜35 | Mpa | |
| -40℃ | ASTM D-638 | Dry｜105 | Mpa | |
| -40℃ | ASTM D-638 | 3.0%Water｜95 | Mpa | |
| IZOD notch impact strength | 23℃ | ASTM D-256 | Dry｜205 | J/m |
| 23℃ | ASTM D-256 | 3.0%Water｜690 | J/m | |
| -40℃ | ASTM D-256 | Dry｜175 | J/m | |
| -40℃ | ASTM D-256 | 3.0%Water｜- | J/m | |
| Taber abraser | 1000Cycles | mg | 6.00到7.00 | -- |
| IZOD notch free impact strength | 23℃ | ASTM D-256 | Dry｜不断裂 | kJ/m² |
| 23℃ | ASTM D-256 | 3.0%Water｜- | kJ/m² | |
| Bending stress | -40°C | MPa | 130 | -- |
| 23°C | MPa | 80.0 | -- | |
| elongation at break | -40℃ | ASTM D-638 | Dry｜15 | % |
| -40℃ | ASTM D-638 | 3.0%Water｜5.0 | % | |
| 23℃ | ASTM D-638 | Dry｜<200 | % | |
| 23℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 80℃ | ASTM D-638 | Dry｜<200 | % | |
| 80℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| Rockwell hardness | ASTM D785 | 114 | ||
| 23℃ | ASTM D-785 | 3.0%Water｜- | R scale | |
| 23℃ | ASTM D-785 | Dry｜114 | R scale | |
| Bending modulus | -40°C | MPa | 2900 | -- |
| 23°C | MPa | 2100 | 700 | |
| 80°C | MPa | 500 | -- | |
| -40℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| 23℃ | ASTM D-790 | Dry｜2.1 | GPa | |
| 23℃ | ASTM D-790 | 3.0%Water｜0.7 | GPa | |
| 80℃ | ASTM D-790 | Dry｜0.5 | GPa | |
| 80℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| -40℃ | ASTM D-790 | Dry｜2.9 | GPa | |
| bending strength | -40℃ | ASTM D-790 | Dry｜130 | Mpa |
| -40℃ | ASTM D-790 | 3.0%Water｜- | Mpa | |
| 23℃ | ASTM D-790 | Dry｜80 | Mpa | |
| 23℃ | ASTM D-790 | 3.0%Water｜- | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.86MPa | ASTM D-648 | 3.0%Water｜- | °C |
| 0.46MPa | ASTM D-648 | Dry｜160 | °C | |
| 0.46MPa | ASTM D-648 | 3.0%Water｜- | °C | |
| 1.86MPa | ASTM D-648 | Dry｜67 | °C | |
| 0.45MPa,Unannealed | °C | 160 | -- | |
| 1.8MPa,Unannealed | °C | 51.0 | -- | |
| melting point | DSC | Dry｜225 | °C | |
| DSC | 3.0%Water｜- | °C | ||
| Linear expansion coefficient | ASTM D-696 | Dry｜8-9 | 10-5/℃ | |
| ASTM D-696 | 3.0%Water｜- | 10-5/℃ | ||
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8.0E-5到9.0E-5 | -- |
| Melting temperature | °C | 225 | -- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 16 | 54 |
| 23°C | 无断裂 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | 114 | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃ | ASTM D-570 | Dry｜8.0 | % |
| 23℃ | ASTM D-570 | 3.0%Water｜- | % | |
| 23℃，24hr | ASTM D-570 | Dry｜1.7 | % | |
| 23℃，24hr | ASTM D-570 | 3.0%Water｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.