PA6 Amilan® CM1001G-20 TORAY JAPAN
165
Unit Price:$2671 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 154.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.29 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.3 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.00mm4 | % | 0.30到0.50 | -- |
| TD:3.00mm3 | % | 0.60到0.90 | -- | |
| Water absorption rate | Saturation,23°C | % | 7.8 | -- |
| 23°C,24hr | % | 1.3 | -- | |
| Enhanced content | 20 | wt% | ||
| Taber wear amount | (1000g,CS-17)23 ℃ | ASTM D-1044 | 12 | mg/1000次 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000Cycles | mg | 0.300 | -- |
| Compressive stress | 80°C | MPa | 90.0 | -- |
| 23°C | MPa | 155 | 80.0 | |
| -40°C | MPa | 240 | -- | |
| shear strength | 23°C | MPa | 115 | 65.0 |
| Friction coefficient vs. Metal5 | 0.15 | -- | ||
| Tensile and flexural strength | 23℃ | ASTM D-638 | 1200 | kg/cm |
| Elongation at break | 23℃ | ASTM D-638 | 5 | % |
| Izod Heng Strike | 23℃ V-Notched1/2 | ASTM D-256 | 6 | kg·cm/cm |
| Tensile stress | 23°C | MPa | 120 | -- |
| Tensile strain | Break,-40°C | % | 2.5 | 3.0 |
| Break,23°C | % | 3.0 | ||
| Break,80°C | % | 5.0 | 5.5 | |
| Rockwell hardness | ASTM D785 | R120,M92 | ||
| R-标度 23℃ | ASTM D-785 | 120 | ||
| M-标度 23℃ | ASTM D-785 | 92 | ||
| Bending modulus | 23°C | MPa | 6800 | 3500 |
| 80°C | MPa | 3200 | 2600 | |
| -40°C | MPa | 8700 | 7300 | |
| Bending stress | -40°C | MPa | 275 | -- |
| 23°C | MPa | 205 | -- | |
| 80°C | MPa | 115 | -- | |
| Flexural strength | 23℃ | ASTM D-790 | 1800 | kg/cm |
| 80℃ | ASTM D-790 | 1000 | kg/cm | |
| -40℃ | ASTM D-790 | 2400 | kg/cm | |
| Flexural modulus | -40℃ | ASTM D-790 | 78000 | kg/cm |
| 80℃ | ASTM D-790 | 29000 | kg/cm | |
| 23℃ | ASTM D-790 | 60000 | kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| specific heat | 0.36 | Cal/g·℃ | ||
| J/kg/°C | 1600 | -- | ||
| thermal conductivity | W/m/K | 0.33 | -- | |
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 215 | -- |
| melting point | 差示扫描测热计DSC | 225 | °C | |
| 225 | ℃（℉） | |||
| heat deflection temperature | 18.6kg/cm | ASTM D-648 | 185 | °C |
| 4.6kg/cm | ASTM D-648 | 215 | °C | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 3E-05 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | ASTM D-696 | 3 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1/8" 短时间 | ASTM D-149 | 20 | KV/mm |
| kV/mm | 20 | -- | ||
| Dissipation factor 6 | 23°C,1MHz | 0.030 | -- | |
| 23°C,1kHz | 0.040 | -- | ||
| 23°C,50Hz | 0.040 | -- | ||
| Arc resistance 7 | sec | 120 | -- | |
| Dielectric constant 6 | 23°C,1MHz | 3.80 | -- | |
| 23°C,1kHz | 4.40 | -- | ||
| 23°C,50Hz | 4.60 | -- | ||
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 | Ω.cm | |
| ohms·cm | 1E+15 | 1E+12 | ||
| ASTM D-257 | 10 | Ω·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 25 | |
| 23°C | kJ/m² | 55 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | 120 | -- | |
| R-Sale,80°C | 12 | -- | ||
| M-Sale,23°C | 92 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24hr 23℃ | ASTM D-570 | 1.3 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.