PP Fibremod™ GB317SF BOREALIS EUROPE
128
- Unit Price:
- $1780 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 2.00 mm | 内部方法 | 1.0 | % |
| Flow : 2.00 mm | 内部方法 | 0.10 | % | |
| Melt flow rate | 230°C/2.16 kg | ISO 1133 | 5.0 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 3 | ISO 178 | 6300 | Mpa | |
| Tensile stress | ISO 527-2/50 | 105 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 160 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Processing (melt) temperature | 230 到 280 | °C | ||
| Mold temperature | 30 到 50 | °C | ||
| Maintain pressure | 30.0 到 60.0 | Mpa | ||
| Hopper temperature | 40 到 80 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA 277 | < 50.0 | µgC/g | |
| Atomization -16 hours | 100°C | DIN 75201 | < 2.0 | mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.