Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 0.900 | g/cm³ |
| Melt mass flow rate | | ASTMD1238 | 9.0 | g/10min |
| Shrinkage rate | MD:2.00mm | 内部方法 | 1.6 | % |
| Shrinkage rate | TD:2.00mm | 内部方法 | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | Yield | ASTMD638 | 27.5 | Mpa |
| Tensile strength | Break | ASTMD638 | 23.0 | Mpa |
| elongation | Break | ASTMD638 | 300 | % |
| Bending modulus | | ASTMD790 | 1290 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 124 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | ASTMD257 | 1E+13 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | -20°C | ASTMD256 | 45 | J/m |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 92 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 91 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| WeatherResistance2 | 63°C | 内部方法 | 1.4 | month |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.