PP 1100N OPP OMAN
130
Unit Price:$1492 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 73.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Homopolymer High temperature resistan high strength
- Application Areas:Household goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 50mm/min | ISO 527 | 36 | Mpa |
| elongation at break | 50mm/min | ISO 527 | 9 | % |
| Bending modulus | 1mm/min | ISO 527 | 1550 | Mpa |
| IZOD notch impact strength | 23℃ | ISO 180/1A | 3.0 | Kj/cm2 |
| ball indentation hardness | H 358/30 | ISO 2039-1 | 76 | Mpa |
| Charpy impact strength | 23℃ | ISO 179/1eU | 110 | Kj/cm2 |
| 0℃ | ISO 179/1eU | 25 | Kj/cm2 | |
| -20℃ | ISO 179/1eU | 14 | Kj/cm2 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa | ISO 75 | 54 | °C |
| 0.45MPa | ISO 75 | 85 | °C | |
| vicat softening point | A/120 10N | ISO 306 | 155 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO 1183 | 0.91 | g/cm³ | |
| Melt index | 230℃，2.16kg | ISO 1133 | 12 | g/10min |
| Shrinkage rate | 1.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.