HIPS STYRON A-TECH 1300 TRINSEO HK
118
- Unit Price:
- $1544 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Flame retardant
- Application Areas:Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | 1.5mm | UL 94 | HB | |
| Density/specific gravity | ASTM D-792 | 1.04 | ||
| Mold shrinkage rate | ASTM D-955 | 0.004-0.007 | cm/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Break | ASTM D-638 | 50 | % |
| Tensile fracture strength | ASTM D-638 | 26 | Mpa | |
| Bending modulus | ASTM D-790 | 2007 | Mpa | |
| Gap impact strength | 23℃ | ASTM D-256 | 128 | J/m |
| Tensile yield strength | ASTM D-638 | 28 | Mpa | |
| bending strength | ASTM D-790 | 50 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.82MPa，经Annealed | ASTM D-648 | 99 | °C |
| 1.82MPa，未经Annealed | 75 | °C | ||
| Linear coefficient of thermal expansion | 10 | 7.6 | cm/cm℃ | |
| vicat softening point | ASTM D-1525 | 105 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 200℃,5Kg | ASTM D-1238 | 4.5 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.