AS(SAN) 80HF LG CHEM KOREA
231
- Unit Price:
- $2210 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting transparent High mobility
- Application Areas:packing Kitchen utensils Electrical/Electronic App Electrical appliances Household fan blades container small home appliances
- Color:--
- Grade:Chemical resistance
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| Water absorption rate | Saturation | ISO622 | 0.16 | % |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 3.0 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 29 | g/10min | |
| 230°C/3.8kg | ASTMD1238 | 10 | g/10min | |
| Density/specific gravity | ASTMD792 | 1.07 | g/cm³ | |
| ISO11832 | 1070 | kg/m3 | ||
| Meltvolume-flowrate | 220°C/10.0kg | ISO11332 | 31.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strain 4 | Break,3.20mm | ASTMD638 | 6.0 | % |
| Bending modulus 5 | 3.20mm | ASTMD790 | 3680 | Mpa |
| Tensile modulus 3 | 3.20mm | ASTMD638 | 3110 | Mpa |
| Tensile strength 4 | Yield,3.20mm | ASTMD638 | 73.5 | Mpa |
| Bending strength 5 | 3.20mm | ASTMD790 | 118 | Mpa |
| Tensile modulus | ISO527-22 | 3300 | Mpa | |
| Tensile stress | Break | ISO527-22 | 70.0 | Mpa |
| Tensile strain | Break | ISO527-22 | 6.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 50.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 50.0 | °C | |
| RTIStr | UL746 | 50.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-22 | 6.7E-05 | cm/cm/°C |
| TD | ISO11359-22 | 6.7E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 90.0 | °C |
| Glass transition temperature 8 | ISO11357-22 | 110 | °C | |
| Vicat softening temperature | ASTMD1525 | 100 | °C | |
| 50N | ISO3062 | 100 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical strength | IEC60243-12 | 51 | KV/mm | |
| Surface resistivity | IEC600932 | >1.0E+15 | ohms | |
| Volume resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Compared to the leakage trace index | IEC601122 | 375 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA2 | 2.00 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C,6.40mm | ASTMD256 | 9.8 | J/m |
| 23°C,6.40mm | ASTMD256 | 9.8 | J/m | |
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | 2.80 | kJ/m² |
| Charpy impact strength | 23°C | ISO179/1eU2 | 13.0 | kJ/m² |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | 4.80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 123 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.2mm | UL94 | HB | ||
| Burning Behav.atthicknessh | 3.20mm,UL | ISO12102 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.