ABS LNP™ STAT-KON™ A3000T SABIC INNOVATIVE US
131
- Unit Price:
- $3429 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 37.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Antistatic transparent
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.08 | g/cm³ | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.80 | % |
| 平衡,23°C,50%RH | ISO62 | 0.80 | % | |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.50to0.70 | % |
| TD：24hr | ASTMD955 | 0.70to0.90 | % | |
| TD:24小时 | ISO294-4 | 0.83 | % | |
| MD:24小时 | ISO294-4 | 0.68 | % | |
| density | ISO1183 | 1.08 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 1220 | Mpa | |
| ISO527-2/1 | 1140 | Mpa | ||
| Tensile strength | 屈服 | ASTMD638 | 32.0 | Mpa |
| Tensile stress | 屈服 | ISO527-2/5 | 32.0 | Mpa |
| Tensile strain | 断裂 | ISO527-2/5 | 63 | % |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 1480 | Mpa |
| ISO178 | 1420 | Mpa | ||
| Bending stress | ISO178 | 42.0 | Mpa | |
| bending strength | 断裂,50.0mm跨距 | ASTMD790 | 42.6 | Mpa |
| Tensile strength | 断裂 | ASTMD638 | 24.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/5 | 24.0 | Mpa |
| elongation | 断裂 | ASTMD638 | 39 | % |
| Tensile strain | 断裂 | ISO527-2 | 63 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 68.0 | °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 81.0 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 81.0 | °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 87.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1.0E+10to1.0E+12 | ohms | |
| Volume resistivity | ASTMD257 | 9.0to11 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 12 | kJ/m² |
| 23°C | ASTMD256 | 130 | J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.