ABS CYCOLAC™ EX58F-NA1000 SABIC INNOVATIVE US
139
- Unit Price:
- $1778 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 24.75MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:Electrical appliances Architectural application Automotive interior parts
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60to0.80 | % |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 4.0 | g/10min |
| MeltViscosity | 240°C,100sec^-1 | ASTMD3835 | 1550 | Pa·s |
| density | ASTMD792 | 1.03 | g/cm³ | |
| ISO1183 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | 断裂 | ASTMD638 | 30.0 | Mpa |
| 屈服 | ASTMD638 | 39.0 | Mpa | |
| Tensile stress | 屈服 | ISO527-2/50 | 41.0 | Mpa |
| 断裂 | ISO527-2/50 | 30.0 | Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 2.6 | % |
| 断裂 | ISO527-2/50 | 21 | % | |
| Tensile modulus | ASTMD638 | 2080 | Mpa | |
| ISO527-2/1 | 1970 | Mpa | ||
| elongation | 屈服 | ASTMD638 | 3.1 | % |
| 断裂 | ASTMD638 | 32 | % | |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2160 | Mpa |
| ISO178 | 2000 | Mpa | ||
| bending strength | ISO178 | 60.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 66.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 91.0 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 76.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 78.0 | °C | |
| RTIElec | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 60.0 | °C | |
| RTIStr | UL746 | 60.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1E-04 | cm/cm/°C |
| TD：-40到40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| Vicat softening temperature | ASTMD152510 | 106 | °C | |
| -- | ISO306/B50 | 95.0 | °C | |
| -- | ISO306/B120 | 97.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 37.0 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 37 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 300 | J/m |
| 23°C | ASTMD256 | 430 | J/m | |
| -30°C | ISO180/1A | 23 | kJ/m² | |
| 23°C | ISO180/1A | 35 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.