ABS CYCOLAC™ FR23 BK4051 SABIC INNOVATIVE US
130
- Unit Price:
- $4513 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High mobility Good flexibility
- Application Areas:--
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 230°C/3.8 kg | ASTM D1238 | 6.8 | g/10 min |
| 220°C/5.0 kg | ISO 1133 | 9.0 | g/10 min | |
| Molten Volume Flow Rate (MVR) | 220°C/10.0 kg | ISO 1133 | 37.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 2410 | Mpa | |
| Elongation rate 3 | Yield | ASTM D638 | 2.1 | % |
| Break | ASTM D638 | 11 | % | |
| Tensile strength 3 | Yield | ASTM D638 | 42.0 | Mpa |
| Break | ASTM D638 | 35.0 | Mpa | |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2720 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 73.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 72.0 | °C | |
| Vicat softening temperature | ASTM D15255 | 90.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.9E-5 | cm/cm/°C | |
| RTI | UL 746 | 60.0 | °C | |
| RTI Imp | UL 746 | 60.0 | °C | |
| RTI Elec | UL 746 | 60.0 | °C |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 310 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Processing (melt) temperature | 200 到 220 | °C | ||
| Mold temperature | 50 到 70 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested injection volume | 50 到 70 | % | ||
| Temperature at the rear of the barrel | 170 到 180 | °C | ||
| Temperature in the middle of the barrel | 195 到 205 | °C | ||
| Temperature at the front of the material cylinder | 200 到 215 | °C | ||
| Spray nozzle temperature | 200 到 220 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 30 到 60 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 41.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.3 mm | UL 94 | V-0 | |
| 2.5 mm | UL 94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.