ABS CYCOLAC™ FR15U BK4051 SABIC INNOVATIVE US
129
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Flame retardant
- Application Areas:Electrical applications Automotive Applications small home appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 230°C/3.8 kg | ASTM D1238 | 3.3 | g/10 min |
| 220°C/5.0 kg | ISO 1133 | 7.0 | g/10 min | |
| Molten Volume Flow Rate (MVR) | 220°C/10.0 kg | ISO 1133 | 40.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2060 | Mpa |
| -- | ISO 527-2/1 | 2210 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 37.0 | Mpa |
| Yield | ISO 527-2/50 | 41.0 | Mpa | |
| Break 3 | ASTM D638 | 30.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 2.4 | % |
| Break 3 | ASTM D638 | 17 | % | |
| Break | ISO 527-2/50 | 22 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2340 | Mpa |
| -- 5 | ISO 178 | 2260 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 63.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 67.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 86.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 75.0 | °C | |
| Vicat softening temperature | -- | 93.0 | °C | |
| -- | ISO 306/B50 | 92.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 9.2E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 85.0 | °C | |
| RTI | UL 746 | 90.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | > 1.0E+14 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Oil | IEC 60243-1 | 20 | KV/mm |
| Arc resistance 9 | ASTM D495 | PLC 7 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | ||
| High arc combustion index (HAI) 10 | UL 746 | PLC 4 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 320 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Suggested injection volume | 50 到 70 | % | ||
| Temperature at the rear of the barrel | 170 到 180 | °C | ||
| Temperature in the middle of the barrel | 200 到 210 | °C | ||
| Temperature at the front of the material cylinder | 205 到 220 | °C | ||
| Spray nozzle temperature | 205 到 230 | °C | ||
| Processing (melt) temperature | 205 到 230 | °C | ||
| Mold temperature | 50 到 70 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 30 到 60 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 28.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| 2.8 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.