ABS POLYLAC® PA-717K ZHENJIANG CHIMEI
141
Unit Price:$2619 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High mobility High gloss High temperature resistan enhance
- Application Areas:fibre
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | --3 | ASTMD792 | 1.04 | g/cm³ |
| 23°C | ISO1183 | 1.04 | g/cm³ | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 1.3 | g/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 | % | |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 16.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield | ISO527-2/50 | 44.0 | Mpa |
| Break | ISO527-2/50 | 33.0 | Mpa | |
| elongation | Break4 | ASTMD638 | 30 | % |
| Break | ISO527-2/50 | 30 | % | |
| Bending modulus | --5 | ASTMD790 | 2410 | Mpa |
| --6 | ISO178 | 1900 | Mpa | |
| bending strength | --5 | ASTMD790 | 70.3 | Mpa |
| --6 | ISO178 | 69.0 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 42.1 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 85.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 82.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 95.0 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 98.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.8E-05 | cm/cm/°C |
| Vicat softening temperature | -- | ISO306/A50 | 103 | °C |
| -- | ASTMD15257 | 104 | °C | |
| Hot deformation temperature | 1.8MPa,Annealed | ISO75-2/A | 97.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 290 | J/m |
| 23°C,6.40mm | ASTMD256 | 250 | J/m | |
| -30°C | ISO180/1A | 12 | kJ/m² | |
| 23°C | ISO180/1A | 25 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 13 | kJ/m² |
| 23°C | ISO179 | 27 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 115 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.