PC/PBT Pocan® DPCF2200 LANXESS GERMANY
148
- Unit Price:
- $3232 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO 60 | 0.8 | g/cm³ | |
| Melt volume flow rate | 260℃，5 kg 260℃/5.0 kg | ISO 1133 | 15 | cm3/10min |
| Shrinkage rate | TD：250℃，2.0 mm Across Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % |
| TD：120℃，2.0 mm，2 hrs Across Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % | |
| MD：250℃，2.0 mm Flow : 482°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % | |
| MD：120℃，2.0 mm，2 hrs Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23℃ 23℃ | ISO 527-1-2 | 2400 | Mpa |
| Tensile strength | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 45 | Mpa |
| Tensile strain | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 2.9 | % |
| Nominal tensile fracture strain | 23℃ 23℃ | ISO 527-2/50 | > 15 | % |
| Bending modulus | 23℃ 23℃ 4 | ISO 178-A | 2500 | Mpa |
| bending strength | 3.50% Strain 3.5% Strain | ISO 178-A | 70 | Mpa |
| 23℃ 23°C | ISO 178 | 75 | Mpa | |
| Bending strain | 5 | % | ||
| Ball pressure hardness | ISO 2039-1 | 104 | Mpa |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 3.3 | |
| 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 2.9 | ||
| Dissipation factor | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 0.025 | |
| 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 0.014 | ||
| Compared to the leakage trace index | Solution A Solution A | IEC 60112 | 300 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30℃ -30°C | ISO 179/1eU | 170 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | No Break | ||
| Impact strength of cantilever beam gap | -30℃ -30°C | ISO 180-1A | < 10 | kJ/m² |
| 0℃ 0°C | ISO 180-1A | 11 | kJ/m² | |
| 23℃ 23°C | ISO 180-1A | 10 | kJ/m² | |
| Cantilever beam without notch impact strength | -30℃ -30°C | ISO 180/1U | 150 | kJ/m² |
| 23℃ 23°C | ISO 180/1U | No Break |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade 0.75 mm | 0.75 mm | UL 94 | V-0 | |
| Flammability index of heating wire | 0.80 mm 0.8 mm | IEC 60695-2-12 | 960 | °C |
| Ignition temperature of heating wire | 0.8 mm 0.8 mm | IEC 60695-2-13 | 800 | °C |
| 1.6 mm 1.6 mm | IEC 60695-2-13 | 800 | °C | |
| 3 mm 3.0 mm | IEC 60695-2-13 | 800 | °C |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa，Unannealed 1.8 MPa，Unannealed | ISO 75-2/A | 75 | °C |
| 0.45 MPa，Unannealed 0.45 MPa，Unannealed | ISO 75-2/B | 95 | °C | |
| Vicat softening temperature | B120 B120 | ISO 306/B120 | 118 | °C |
| Ball pressure test | 115℃ 115℃ | IEC 60695-10-2 | Pass | |
| Melting temperature | ISO 11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | TD：23~55℃ TD：23 to 55℃ | ISO 11359-2 | 0.00010 | 1/℃ |
| MD：23~55℃ MD：23 to 55℃ | ISO 11359-2 | 0.000080 | 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.