PPO/PA NORYL GTX™ GTX979-74709 SABIC INNOVATIVE US
209
- Unit Price:
- $5481 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility dimensional stability High temperature resistan Hydrolysis resistance
- Application Areas:Electrical applications Industrial machinery Application in the automo
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 15 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 11.0 | cm3/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 1.2到1.6 | % |
| TD:3.20mm | 内部方法 | 1.2到1.6 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 4.2 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --3 | ASTMD638 | 2000 | Mpa |
| -- | ISO527-2/1 | 2100 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 55.0 | Mpa |
| Yield | ISO527-2/50 | 55.0 | Mpa | |
| Break4 | ASTMD638 | 50.0 | Mpa | |
| Break | ISO527-2/50 | 50.0 | Mpa | |
| elongation | Yield4 | ASTMD638 | 5.0 | % |
| Yield | ISO527-2/50 | 4.0 | % | |
| Break4 | ASTMD638 | 60 | % | |
| Break | ISO527-2/50 | 30 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2050 | Mpa |
| --6 | ISO178 | 2150 | Mpa | |
| Bending stress | --6,7 | ISO178 | 80.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 80.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan10 | ISO75-2/Be | 178 | °C |
| Vicat softening temperature | -- | ASTMD152511,ISO306/B5011 | 180 | °C |
| -- | ISO306/B120 | 182 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 9.5E-05 | cm/cm/°C |
| MD:23to80°C | ISO11359-2 | 9.6E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD:23to80°C | ISO11359-2 | 9.6E-05 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 185 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 内部方法 | 1.0E+3到1.0E+4 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 12 | kJ/m² |
| 23°C | ISO179/1eA | 20 | kJ/m² | |
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | 无断裂 | |
| 23°C | ISO180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 3.2mm | IEC60695-2-12 | 650 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.